PA66 R533H 含33%玻纤增强,热稳定,润滑
Vydyne® R533H
聚酰胺66
玻璃纤维33%增强材料
Ascend Performance Materials LLC.
产品说明
The Vydyne R533® Series of 33% glass fiber reinforced nylons are available in natural,black and heat stabilized versions. They are general purpose,injection molding grades which are lubricated for good machine feed,flow and mold release.
Vydyne R533 Series resins are members of a wide range of glass reinforced resins supplied by Ascend Performance Materials. Other glass fiber loadings available include 13% and 43%.
Vydyne R533 Series resins have tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs,energy consumption,and part weight are key advantages of Vydyne glass reinforced Nylon 6,6 resins over aluminum and/or zinc die cast parts.
Vydyne R533H is a heat stabilized grade,formulated to minimize the oxidative and thermal degradation of the nylon polymer when exposed to elevated temperatures for extended periods of time. Vydyne R533H provides improved retention of physical properties under exposure to long-term heat. The continuous operating use temperature is 275℉ and short-term peak temperatures as high as 475℉.
含添加剂：热稳定剂、润滑剂
填料增强：含33%玻璃纤维增强
材料特点：刚性高、高强度、经润滑、良好的流动性、热稳定性、脱模性能良好
材料用途：齿轮、动力/其它工具、汽车的发动机罩下的零件
ul 档案号：E70062
材料外观：黑色、自然色
产品牌号：PA66 R533H
产品形式：颗粒料
加工方法：注射成型
物料数据
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
密度 |
1.4 |
-- |
g/cm3 |
ISO 1183 |
|
收缩率 |
|
|
|
ISO 294-4 |
|
横向流量:23℃,2.00 mm |
0.9 |
-- |
% |
|
|
流量:23℃,2.00 mm |
0.4 |
-- |
% |
|
|
吸水率 |
|
|
|
ISO 62 |
|
23℃,24 hr |
0.8 |
-- |
% |
|
|
平衡,23℃,50% RH |
1.8 |
-- |
% |
|
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
10200 |
7900 |
MPa |
ISO 527-2 |
|
拉伸应力(断裂,23℃) |
205 |
148 |
MPa |
ISO 527-2 |
|
拉伸应变(断裂,23℃) |
3 |
5 |
% |
ISO 527-2 |
|
弯曲模量(23℃) |
9700 |
6500 |
MPa |
ISO 178 |
|
弯曲强度(23℃) |
290 |
205 |
MPa |
ISO 178 |
|
泊松比 |
0.4 |
-- |
|
ISO 527-2 |
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
|
ISO 179 |
|
-30℃ |
12 |
-- |
kJ/m2 |
|
|
23℃ |
12 |
-- |
kJ/m2 |
|
|
简支梁缺口冲击强度 |
|
|
|
ISO 179 |
|
-30℃ |
75 |
-- |
kJ/m2 |
|
|
23℃ |
85 |
-- |
kJ/m2 |
|
|
悬壁梁缺口冲击强度(23℃) |
12 |
-- |
kJ/m2 |
ISO 180 |
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
|
0.45 MPa,未退火 |
260 |
-- |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
250 |
-- |
℃ |
ISO 75-2/A |
|
维卡软化温度 |
252 |
-- |
℃ |
ISO 306/B |
|
溶融温度(DSC) |
260 |
-- |
℃ |
ISO 3146 |
|
线形膨胀系数 |
|
|
|
ISO 11359-2 |
|
流动:23 到 55℃,2.00 mm |
2.1E-5 |
-- |
cm/cm/℃ |
|
|
横向:23 到 55℃,2.00 mm |
1.1E-4 |
-- |
cm/cm/℃ |
|
|
RTI Elec |
|
|
|
UL 746 |
|
0.750 mm |
140 |
-- |
℃ |
|
|
1.50 mm |
140 |
-- |
℃ |
|
|
3.00 mm |
140 |
-- |
℃ |
|
|
RTI Imp |
|
|
|
UL 746 |
|
0.750 mm |
125 |
-- |
℃ |
|
|
1.50 mm |
125 |
-- |
℃ |
|
|
3.00 mm |
125 |
-- |
℃ |
|
|
RTI Str |
|
|
|
UL 746 |
|
0.750 mm |
140 |
-- |
℃ |
|
|
1.50 mm |
140 |
-- |
℃ |
|
|
3.00 mm |
140 |
-- |
℃ |
|
|
电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
体积电阻率(3.00 mm) |
3.0E+15 |
-- |
ohm·cm |
IEC 60093 |
|
耐电强度2(23℃,3.00 mm) |
16 |
-- |
kV/mm |
IEC 60243-1 |
|
耐电弧性(3.00 mm) |
PLC 6 |
-- |
|
ASTM D495 |
|
相比耐漏电起痕指数(CTI)(3.00 mm) |
PLC 2 |
-- |
|
UL 746 |
|
漏电起痕指数(3.00 mm) |
400 到 599 |
-- |
V |
IEC 60112 |
|
高电弧燃烧指数(HAI) |
|
|
|
UL 746 |
|
0.750 mm |
PLC 0 |
-- |
|
|
|
1.50 mm |
PLC 0 |
-- |
|
|
|
3.00 mm |
PLC 0 |
-- |
|
|
|
高电压电弧起痕速率(HVTR)(3.00 mm) |
PLC 1 |
-- |
|
UL 746 |
|
热丝引燃(HWI) |
|
|
|
UL 746 |
|
0.750 mm |
PLC 4 |
-- |
|
|
|
1.50 mm |
PLC 3 |
-- |
|
|
|
3.00 mm |
PLC 4 |
-- |
|
|
|
可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
|
UL 94 |
|
0.750 mm,All colors |
HB |
-- |
|
|
|
1.50 mm,All colors |
HB |
-- |
|
|
|
3.00 mm,All colors |
HB |
-- |
|
|
|
极限氧指数 |
28 |
-- |
% |
ASTM D2863 |
|
注射 |
干燥 |
单位制 |
||
|
干燥温度 |
< 70.0 |
℃ |
||
|
干燥时间 |
1.0 到 3.0 |
hr |
||
|
建议注入量 |
40 到 80 |
% |
||
|
建议的最大回制料比例 |
25 |
% |
||
|
螺筒后部温度 |
280 到 310 |
℃ |
||
|
螺筒中部温度 |
280 到 310 |
℃ |
||
|
螺筒前部温度 |
280 到 310 |
℃ |
||
|
射嘴温度 |
280 到 310 |
℃ |
||
|
加工(熔体)温度 |
285 到 305 |
℃ |
||
|
模具温度 |
65.0 到 95.0 |
℃ |
||
|
注塑温度 |
55.0 到 140 |
MPa |
||
|
注射速度 |
快速 |
|
||
|
保压 |
55.0 到 140 |
MPa |
||
|
背压 |
0.200 到 1.00 |
MPa |
||
|
螺杆转速 |
60 到 120 |
rpm |
||
|
合模力 |
2.7 到 6.2 |
kN/cm2 |
||
|
垫层 |
3.00 到 6.40 |
mm |
||