PA66 R533H BK02 加33%玻璃纤增强,高流动,热稳定 润滑
Vydyne® R533H BK02
33%玻璃纤维增强材料
聚酰胺66
Ascend Performance Materials Operations LLC
产品说明:
Vydyne R533H BK02 is 33% glass-fiber reinforced, heat-stabilized PA66 resin. Available in black, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is lubricated for improved machine feed and flow.
Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Vydyne R533H BK02 resin is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R533H BK02 resin has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions.
Typical Applications/End Uses:
Vydyne R533H BK02 resin has been used for many under-the-hood automotive applications, motor housings for power tools and garden appliances. This resin has also been used in miscellaneous brackets, gears and clips that require high rigidity and strength.
黄卡下载：E70062-249084
填料增强：含33%玻璃纤维增强
含添加剂：热稳定剂，润滑剂
材料特性：高刚性，高强度，流动性高，热稳定，润滑，脱模性能良好
材料用途：齿轮，动力/其它工具，汽车的发动机罩下的零件，外壳
加工方法：注射成型
产品外观：黑色粒子
塑料牌号：PA66 R533H BK02
产品物性：
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
密度 |
1.40 |
-- |
g/cm³ |
ISO 1183 |
|
收缩率 |
|
|
|
ISO 294-4 |
|
垂直流动方向:23℃,2.00 mm |
0.90 |
-- |
% |
|
|
流动方向:23℃,2.00 mm |
0.40 |
-- |
% |
|
|
吸水率 |
|
|
|
ISO 62 |
|
23℃,24 hr |
0.80 |
-- |
% |
|
|
平衡,23℃,50% RH |
1.7 |
-- |
% |
|
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
10600 |
7900 |
MPa |
ISO 527-2 |
|
拉伸应力(断裂,23℃) |
205 |
145 |
MPa |
ISO 527-2 |
|
拉伸应变(断裂,23℃) |
3.0 |
5.0 |
% |
ISO 527-2 |
|
弯曲模量(23℃) |
10200 |
6500 |
MPa |
ISO 178 |
|
弯曲应力(23℃) |
290 |
200 |
MPa |
ISO 178 |
|
泊松比 |
0.40 |
-- |
|
ISO 527-2 |
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
|
ISO 179/1eA |
|
-30℃ |
10 |
12 |
kJ/m² |
|
|
23℃ |
11 |
14 |
kJ/m² |
|
|
简支梁无缺口冲击强度 |
|
|
|
ISO 179/1eU |
|
-30℃ |
70 |
85 |
kJ/m² |
|
|
23℃ |
80 |
90 |
kJ/m² |
|
|
悬壁梁缺口冲击强度 |
|
|
|
ISO 180 |
|
-30℃ |
10 |
12 |
kJ/m² |
|
|
23℃ |
12 |
14 |
kJ/m² |
|
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
|
0.45 MPa,未退火 |
260 |
-- |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
250 |
-- |
℃ |
ISO 75-2/A |
|
熔融温度 |
260 |
-- |
℃ |
ISO 11357-3 |
|
线形热膨胀系数 |
|
|
|
ISO 11359-2 |
|
流动:23 到 55℃,2.00 mm |
2.1E-5 |
-- |
cm/cm/℃ |
|
|
横向:23 到 55℃,2.00 mm |
1.1E-4 |
-- |
cm/cm/℃ |
|
|
RTI Elec |
|
|
|
UL 746 |
|
0.750 mm |
140 |
-- |
℃ |
|
|
1.50 mm |
140 |
-- |
℃ |
|
|
3.00 mm |
140 |
-- |
℃ |
|
|
RTI Imp |
|
|
|
UL 746 |
|
0.750 mm |
125 |
-- |
℃ |
|
|
1.50 mm |
125 |
-- |
℃ |
|
|
3.00 mm |
125 |
-- |
℃ |
|
|
RTI |
|
|
|
UL 746 |
|
0.750 mm |
140 |
-- |
℃ |
|
|
1.50 mm |
140 |
-- |
℃ |
|
|
3.00 mm |
140 |
-- |
℃ |
|
|
电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
体积电阻率(0.750 mm) |
1.0E+13 |
-- |
ohm·cm |
IEC 60093 |
|
介电强度(1.00 mm) |
20 |
-- |
kV/mm |
IEC 60243 |
|
耐电弧性(3.00 mm) |
PLC 6 |
-- |
|
ASTM D495 |
|
漏电起痕指数(3.00 mm) |
250 到 399 |
-- |
V |
IEC 60112 |
|
高电弧燃烧指数(HAI) |
|
|
|
UL 746 |
|
0.750 mm |
PLC 0 |
-- |
|
|
|
1.50 mm |
PLC 0 |
-- |
|
|
|
3.00 mm |
PLC 0 |
-- |
|
|
|
高电压电弧起痕速率 (HVTR) |
PLC 1 |
-- |
|
UL 746 |
|
热丝引燃 (HWI) |
|
|
|
UL 746 |
|
0.750 mm |
PLC 4 |
-- |
|
|
|
1.50 mm |
PLC 3 |
-- |
|
|
|
3.00 mm |
PLC 4 |
-- |
|
|
|
可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
|
UL 94 |
|
0.750 mm |
HB |
-- |
|
|
|
1.50 mm |
HB |
-- |
|
|
|
3.00 mm |
HB |
-- |
|
|
|
灼热丝易燃指数 |
|
|
|
IEC 60695-2-12 |
|
0.750 mm |
675 |
-- |
℃ |
|
|
1.50 mm |
675 |
-- |
℃ |
|
|
3.00 mm |
675 |
-- |
℃ |
|
|
热灯丝点火温度 |
|
|
|
IEC 60695-2-13 |
|
0.750 mm |
700 |
-- |
℃ |
|
|
1.50 mm |
700 |
-- |
℃ |
|
|
3.00 mm |
700 |
-- |
℃ |
|
|
注射 |
干燥 |
单位制 |
||
|
干燥温度 |
80.0 |
℃ |
||
|
干燥时间 |
4.0 |
hr |
||
|
建议的最大回制料比例 |
25 |
% |
||
|
料筒后部温度 |
280 到 310 |
℃ |
||
|
料筒中部温度 |
280 到 310 |
℃ |
||
|
料筒前部温度 |
280 到 310 |
℃ |
||
|
射嘴温度 |
280 到 310 |
℃ |
||
|
加工（熔体）温度 |
285 到 305 |
℃ |
||
|
模具温度 |
65.0 到 95.0 |
℃ |
||