PA66 R535 加35%玻璃纤增强,耐汽油 耐水解 润滑,抗溶剂尼龙
Vydyne® R535
35%玻璃纤维增强材料
聚酰胺66
Ascend Performance Materials Operations LLC
产品说明:
Vydyne R535 is general-purpose, hydrolysis-resistant, 35% glass-fiber reinforced PA66 resin. This product is lubricated for improved flow and offers superior surface appearance.
Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Typical Applications/End Uses:
To come
黄卡下载：E70062-100521434
填料增强：含35%玻璃纤维增强
含添加剂：润滑剂
材料特性：抗冻，抗溶剂，良好的流动性，耐化学，耐疲劳，耐汽油，耐水解，润滑
加工方法：注射成型
产品外观：自然色粒子
塑料牌号：PA66 R535
产品物性：
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
密度(23℃) |
1.41 |
-- |
g/cm³ |
ISO 1183 |
|
收缩率 |
|
|
|
ISO 294-4 |
|
垂直流动方向 :2.00 mm |
0.90 |
-- |
% |
|
|
流动方向 :2.00 mm |
0.40 |
-- |
% |
|
|
吸水率 |
|
|
|
ISO 62 |
|
23℃, 24 hr |
0.80 |
-- |
% |
|
|
平衡, 23℃,50% RH |
1.6 |
-- |
% |
|
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
11600 |
8500 |
MPa |
ISO 527-2 |
|
拉伸应力(断裂, 23℃) |
210 |
150 |
MPa |
ISO 527-2 |
|
拉伸应变(断裂, 23℃) |
3.0 |
5.0 |
% |
ISO 527-2 |
|
弯曲模量(23℃) |
10500 |
7000 |
MPa |
ISO 178 |
|
弯曲应力(23℃) |
300 |
205 |
MPa |
ISO 178 |
|
泊松比(23℃) |
0.4 |
-- |
|
ISO 527 |
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
|
ISO 179/1eA |
|
-30℃ |
11 |
12 |
kJ/m² |
|
|
23℃ |
12 |
14 |
kJ/m² |
|
|
简支梁无缺口冲击强度 |
|
|
|
ISO 179/1eU |
|
-30℃ |
70 |
85 |
kJ/m² |
|
|
23℃ |
80 |
90 |
kJ/m² |
|
|
悬壁梁缺口冲击强度 |
|
|
|
ISO 180 |
|
-30℃ |
11 |
12 |
kJ/m² |
|
|
23℃ |
12 |
14 |
kJ/m² |
|
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
|
0.45 MPa,未退火 |
260 |
-- |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
250 |
-- |
℃ |
ISO 75-2/A |
|
熔融温度 |
260 |
-- |
℃ |
ISO 11357-3 |
|
线形热膨胀系数 |
|
|
|
ISO 11359-2 |
|
流动: 23 到 55℃ |
2.0E-5 |
-- |
cm/cm/℃ |
|
|
横向: 23 到 55℃ |
1.1E-4 |
-- |
cm/cm/℃ |
|
|
RTI Elec |
|
|
|
UL 746 |
|
0.750 mm |
120 |
-- |
℃ |
|
|
1.50 mm |
120 |
-- |
℃ |
|
|
3.00 mm |
120 |
-- |
℃ |
|
|
RTI Imp |
|
|
|
UL 746 |
|
0.750 mm |
85 |
-- |
℃ |
|
|
1.50 mm |
85 |
-- |
℃ |
|
|
3.00 mm |
105 |
-- |
℃ |
|
|
RTI |
|
|
|
UL 746 |
|
0.750 mm |
115 |
-- |
℃ |
|
|
1.50 mm |
120 |
-- |
℃ |
|
|
3.00 mm |
120 |
-- |
℃ |
|
|
电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
体积电阻率(0.750 mm) |
1.0E+13 |
-- |
ohm·cm |
IEC 60093 |
|
介电强度(1.00 mm) |
24 |
-- |
kV/mm |
IEC 60243 |
|
耐电弧性(3.00 mm) |
PLC 5 |
-- |
|
ASTM D495 |
|
漏电起痕指数(3.00 mm) |
600 |
-- |
V |
IEC 60112 |
|
高电弧燃烧指数(HAI) |
|
|
|
UL 746 |
|
0.750 mm |
PLC 0 |
-- |
|
|
|
1.50 mm |
PLC 0 |
-- |
|
|
|
3.00 mm |
PLC 0 |
-- |
|
|
|
高电压电弧起痕速率 (HVTR) |
PLC 1 |
-- |
|
UL 746 |
|
热丝引燃 (HWI) |
|
|
|
UL 746 |
|
0.750 mm |
PLC 4 |
-- |
|
|
|
1.50 mm |
PLC 4 |
-- |
|
|
|
3.00 mm |
PLC 4 |
-- |
|
|
|
可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
|
UL 94 |
|
0.750 mm |
HB |
-- |
|
|
|
1.50 mm |
HB |
-- |
|
|
|
3.00 mm |
HB |
-- |
|
|
|
补充信息 |
干燥 |
调节后的 |
测试方法 |
|
|
Automotive Materials - (thickness d = 1mm) |
+ |
-- |
FMVSS 302 |
|
|
注射 |
干燥 |
单位制 |
||
|
干燥温度 |
80.0 |
℃ |
||
|
干燥时间 |
4.0 |
hr |
||
|
建议的最大回制料比例 |
25 |
% |
||
|
料筒后部温度 |
280 到 310 |
℃ |
||
|
料筒中部温度 |
280 到 310 |
℃ |
||
|
料筒前部温度 |
280 到 310 |
℃ |
||
|
射嘴温度 |
280 到 310 |
℃ |
||
|
加工（熔体）温度 |
285 到 305 |
℃ |
||
|
模具温度 |
65.0 到 95.0 |
℃ |
||