PET 130 FR BK-112 加玻纤30%增强,阻燃V0级
Petra® PET 130 FR BK-112
30%玻璃纤维增强材料
PET
聚对苯二甲酸乙二醇酯
BASF Corporation
产品说明:
Petra 130 FR BK-112 is a 30% glass fiber reinforced, black pigmented, flame retardant injection molding compound based on post-consumer and post-industrial recycle polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories.
Applications
Petra 130 FR BK-112 is generally recommended for applications such as electrical housing and bobbins.
黄卡下载：E36632-231235
填料增强：含30%玻璃纤维增强材料
材料特性：阻燃级
材料用途：电器外壳，线轴
加工方法：注射成型
产品颜色：黑色粒子
塑料牌号：PET 130 FR BK-112
产品物性：
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.68 |
g/cm³ |
ASTM D792 |
|
收缩率 - 流动(3.18 mm) |
0.30 |
% |
|
|
硬度 |
额定值 |
单位制 |
测试方法 |
|
洛氏硬度(R 级) |
118 |
|
ASTM D785 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
抗张强度 |
|
|
ASTM D638 |
|
断裂,-40℃ |
170 |
MPa |
|
|
断裂,23℃ |
125 |
MPa |
|
|
断裂,80℃ |
75.0 |
MPa |
|
|
断裂,121℃ |
50.0 |
MPa |
|
|
伸长率 |
|
|
ASTM D638 |
|
断裂,-40℃ |
1.7 |
% |
|
|
断裂,23℃ |
2.0 |
% |
|
|
断裂,80℃ |
4.4 |
% |
|
|
断裂,121℃ |
5.6 |
% |
|
|
弯曲模量(23℃) |
9700 |
MPa |
ASTM D790 |
|
弯曲强度(23℃) |
210 |
MPa |
ASTM D790 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度(23℃) |
85 |
J/m |
ASTM D256 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
熔融峰值温度 |
245 |
℃ |
ASTM D3418 |
|
线形热膨胀系数 - 流动 |
2.4E-5 |
cm/cm/℃ |
ASTM E831 |
|
RTI Elec |
|
|
UL 746 |
|
0.300 mm |
75.0 |
℃ |
|
|
0.750 mm |
155 |
℃ |
|
|
1.50 mm |
155 |
℃ |
|
|
3.00 mm |
155 |
℃ |
|
|
RTI Imp |
|
|
UL 746 |
|
0.300 mm |
75.0 |
℃ |
|
|
0.750 mm |
155 |
℃ |
|
|
1.50 mm |
155 |
℃ |
|
|
3.00 mm |
155 |
℃ |
|
|
RTI |
|
|
UL 746 |
|
0.300 mm |
75.0 |
℃ |
|
|
0.750 mm |
155 |
℃ |
|
|
1.50 mm |
155 |
℃ |
|
|
3.00 mm |
155 |
℃ |
|
|
可燃性 |
额定值 |
|
测试方法 |
|
UL 阻燃等级 |
|
|
UL 94 |
|
0.300 mm |
V-0 |
|
|
|
0.750 mm |
V-0 |
|
|
|
5VA |
|
||
|
1.50 mm |
V-0 |
|
|
|
5VA |
|
||
|
3.00 mm |
V-0 |
|
|
|
5VA |
|
||
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
120 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.020 |
% |
|
|
加工（熔体）温度 |
280 到 300 |
℃ |
|
|
模具温度 |
100 到 110 |
℃ |
|
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
|
|