佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PET 130 FR 加玻纤30%增强,阻燃V0级
Petra® PET 130 FR
30%玻璃纤维增强材料
PET
聚对苯二甲酸乙二醇酯
BASF Corporation
产品说明:
Petra 130 FR is a 30% glass fiber reinforced, flame retardant injection molding compound based on post-consumer and post-industrial recycle polyethylene terephthalate feedstocks. It is recognized as UL 94V-0/5VA by Underwriters Laboratories. It is also available in pigmented versions.
Applications
Petra 130 FR is generally recommended for applications such as electrical housing and bobbins.
黄卡下载：E36632-231235
填料增强：含30%玻璃纤维增强材料
材料特性：阻燃级
材料用途：电器外壳，线轴
加工方法：注射成型
产品颜色：可用颜色
塑料牌号：PET 130 FR
产品物性：
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.68 |
g/cm³ |
ASTM D792,ISO 1183 |
|
收缩率 - 流动(3.18 mm) |
0.30 |
% |
|
|
硬度 |
额定值 |
单位制 |
测试方法 |
|
洛氏硬度(R 级) |
118 |
|
ASTM D785 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
11100 |
MPa |
ISO 527-2 |
|
抗张强度(断裂,23℃) |
130 |
MPa |
ASTM D638,ISO 527-2 |
|
伸长率(断裂,23℃) |
2.0 |
% |
ASTM D638,ISO 527-2 |
|
弯曲模量 |
|
|
ASTM D790 |
|
-40℃ |
12400 |
MPa |
|
|
23℃ |
9700 |
MPa |
|
|
121℃ |
2970 |
MPa |
|
|
弯曲强度 |
|
|
ASTM D790 |
|
-40℃ |
275 |
MPa |
|
|
23℃ |
210 |
MPa |
|
|
121℃ |
85.0 |
MPa |
|
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度(23℃) |
90 |
J/m |
ASTM D256 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
0.45 MPa,未退火 |
240 |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
220 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火 |
210 |
℃ |
ISO 75-2/A |
|
熔融峰值温度 |
245 |
℃ |
ASTM D3418,ISO 3146 |
|
线形热膨胀系数 - 流动 |
2.4E-5 |
cm/cm/℃ |
ASTM E831 |
|
RTI Elec |
|
|
UL 746 |
|
0.300 mm |
75.0 |
℃ |
|
|
0.750 mm |
155 |
℃ |
|
|
1.50 mm |
155 |
℃ |
|
|
3.00 mm |
155 |
℃ |
|
|
RTI Imp |
|
|
UL 746 |
|
0.300 mm |
75.0 |
℃ |
|
|
0.750 mm |
155 |
℃ |
|
|
1.50 mm |
155 |
℃ |
|
|
3.00 mm |
155 |
℃ |
|
|
RTI |
|
|
UL 746 |
|
0.300 mm |
75.0 |
℃ |
|
|
0.750 mm |
155 |
℃ |
|
|
1.50 mm |
155 |
℃ |
|
|
3.00 mm |
155 |
℃ |
|
|
电气性能 |
额定值 |
单位制 |
测试方法 |
|
体积电阻率 |
|
|
|
|
1.50 mm |
> 1.0E+13 |
ohm·cm |
ASTM D257 |
|
-- |
> 1.0E+13 |
ohm·cm |
IEC 60093 |
|
介电强度 |
|
|
|
|
1.50 mm3 |
22 |
kV/mm |
ASTM D149 |
|
-- |
40 |
kV/mm |
IEC 60243-1 |
|
介电常数 |
|
|
IEC 60250 |
|
100 Hz |
3.80 |
|
|
|
1 MHz |
3.60 |
|
|
|
耗散因数 |
|
|
IEC 60250 |
|
100 Hz |
0.020 |
|
|
|
1 MHz |
0.020 |
|
|
|
可燃性 |
额定值 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
UL 94 |
|
0.300 mm |
V-0 |
|
|
|
0.750 mm |
V-0 |
|
|
|
5VA |
|
||
|
1.50 mm |
V-0 |
|
|
|
5VA |
|
||
|
3.00 mm |
V-0 |
|
|
|
5VA |
|
||
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
120 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.020 |
% |
|
|
加工（熔体）温度 |
280 到 300 |
℃ |
|
|
模具温度 |
100 到 110 |
℃ |
|
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
|
|
|
备注 |
|||