PET 130 BK-112 加玻璃纤维30%增强
Petra® PET 130 BK-112
30%玻璃纤维增强材料
PET
聚对苯二甲酸乙二醇酯
BASF Corporation
产品说明:
Petra 130 BK-112 is a 30% glass fiber reinforced, black pigmented polyethylene terephthalate injection molding compound. It exhibits a superb combination of performance properties including good strength and stiffness at elevated temperatures. It also has good chemical resistance and dimensional stability, and adequate ductility for most applications.
Applications
Petra 130 BK-112 is generally recommended for applications such as automotive door lock components, housings, gears and electrical and mechanical components.
黄卡下载：E36632-231234
填料增强：含30%玻璃纤维增强材料
材料特性：尺寸稳定性良好，刚性良好，良好的强度，耐化学性良好
材料用途：齿轮，电气元件，机器/机械部件，汽车领域的应用，外壳
加工方法：注射成型
产品颜色：黑色粒子
塑料牌号：PET 130 BK-112
产品物性：
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.55 |
g/cm³ |
ASTM D792,ISO 1183 |
|
收缩率 - 流动(3.18 mm) |
0.40 |
% |
|
|
硬度 |
额定值 |
单位制 |
测试方法 |
|
洛氏硬度(R 级) |
118 |
|
ASTM D785 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
10200 |
MPa |
ISO 527-2 |
|
抗张强度 |
|
|
|
|
断裂,23℃ |
145 |
MPa |
ASTM D638,ISO 527-2 |
|
断裂,-40℃ |
211 |
MPa |
ISO 527-2 |
|
断裂,121℃ |
54.0 |
MPa |
ISO 527-2 |
|
伸长率(断裂,23℃) |
3.0 |
% |
ASTM D638,ISO 527-2 |
|
弯曲模量 |
|
|
|
|
23℃ |
8760 |
MPa |
ASTM D790 |
|
23℃ |
8250 |
MPa |
ISO 178 |
|
弯曲强度(23℃) |
230 |
MPa |
ASTM D790 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
ISO 179 |
|
-30℃ |
8.5 |
kJ/m² |
|
|
23℃ |
9.0 |
kJ/m² |
|
|
悬壁梁缺口冲击强度 |
|
|
|
|
23℃ |
95 |
J/m |
ASTM D256 |
|
-40℃ |
8.5 |
kJ/m² |
ISO 180 |
|
23℃ |
9.5 |
kJ/m² |
ISO 180 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
载荷下热变形温度 |
|
|
|
|
0.45 MPa,未退火 |
235 |
℃ |
ASTM D648 |
|
0.45 MPa,未退火 |
240 |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
215 |
℃ |
ASTM D648 |
|
1.8 MPa,未退火 |
210 |
℃ |
ISO 75-2/A |
|
熔融峰值温度 |
245 |
℃ |
ASTM D3418,ISO 3146 |
|
线形热膨胀系数 - 流动 |
2.3E-5 |
cm/cm/℃ |
ASTM E831 |
|
RTI Elec |
|
|
UL 746 |
|
0.750 mm |
140 |
℃ |
|
|
1.50 mm |
140 |
℃ |
|
|
3.00 mm |
140 |
℃ |
|
|
RTI Imp |
|
|
UL 746 |
|
0.750 mm |
140 |
℃ |
|
|
1.50 mm |
140 |
℃ |
|
|
3.00 mm |
140 |
℃ |
|
|
RTI |
|
|
UL 746 |
|
0.750 mm |
140 |
℃ |
|
|
1.50 mm |
140 |
℃ |
|
|
3.00 mm |
140 |
℃ |
|
|
电气性能 |
额定值 |
单位制 |
测试方法 |
|
体积电阻率 |
|
|
|
|
1.50 mm |
> 1.0E+13 |
ohm·cm |
ASTM D257 |
|
-- |
> 1.0E+13 |
ohm·cm |
IEC 60093 |
|
可燃性 |
额定值 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
UL 94 |
|
0.750 mm |
HB |
|
|
|
1.50 mm |
HB |
|
|
|
3.00 mm |
HB |
|
|
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
120 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.020 |
% |
|
|
加工（熔体）温度 |
280 到 300 |
℃ |
|
|
模具温度 |
100 到 110 |
℃ |
|
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
|
|