PPS 6850L6 含50%玻璃矿物填充
FORTRON® 6850L6 SD3002 BLACK
FORTRON® 6850L6 SF3001 NATURAL
FORTRON 6850L6 | PPS | Mineral / Glass Reinforced
Description
Fortron 6850L6 offers the lowest warpage available. The easy flowing nature allows this product to be injection molded into thin walled applications. The excellent balance of mineral and glass fibers result in a superior heat resistance and dimensional stability. This grade is inherently flame-retardant along with high hardness and rigidity. Especially used for thin walled by unfavorable flow length-wall thickness ratio. This is the most isotropic grade available.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1800 |
kg/m³ |
ISO 1183 |
|
Mold shrinkage - parallel |
0.3 - 0.6 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
0.4 - 0.6 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
18500 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
125 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
16800 |
MPa |
ISO 178 |
|
|
Flexural stress @ break |
190 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
16 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
16 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
4 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
4 |
kJ/m² |
ISO 179/1eA |
|
|
Unnotched impact str (Izod) @ 23℃ |
20 |
kJ/m² |
ISO 180/1U |
|
|
Notched impact strength (Izod) @ 23℃ |
4 |
kJ/m² |
ISO 180/1A |
|
|
Notched impact strength (Izod) @-30℃ |
4 |
kJ/m² |
ISO 180/1A |
|
|
Rockwell hardness |
96 |
M-Scale |
ISO 2039-2 |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
280 |
℃ |
ISO 11357-1,-2,-3 |
|
|
Glass transition temperature (10℃/min) |
90 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
270 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
215 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.15 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.31 |
E-4/℃ |
ISO 11359-2 |
|
|
Flammability @1.6mm nom. thickn. |
V-0 |
class |
UL94 |
|
|
thickness tested (1.6) |
1.5 |
mm |
UL94 |
|
|
Flammability at thickness h |
V-0 |
class |
UL94 |
|
|
thickness tested (h) |
0.38 |
mm |
UL94 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Dissipation factor - 10kHz |
10 |
E-4 |
IEC 60250 |
|
|
Dissipation factor - 1 MHz |
10 |
E-4 |
IEC 60250 |
|
|
Volume resistivity |
>1E13 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
>1E15 |
Ohm |
IEC 60093 |
|
|
Electric strength |
25 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
225 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Injection molding melt temperature |
310 - 340 |
℃ |
ISO 294 |
|
|
Injection molding mold temperature |
135 - 160 |
℃ |
ISO 294 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3 - 4
Drying temperature (℃):130 - 140