PPS FX4330T7 玻璃纤维30%增强
FORTRON® FX4330T7 SD3002 BLACK
FORTRON FX4330T7 | PPS | Impact Modified
Description
FX4330T7 is a 30% glass-fiber reinforced, impact modified injection molding grade offering high flow. Recommended processing conditions are identical to standard filled grades.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1470 |
kg/m³ |
ISO 1183 |
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
9800 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
137 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1.9 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
9000 |
MPa |
ISO 178 |
|
|
Flexural strength (23℃) |
200 |
MPa |
ISO 178 |
|
|
Unnotched impact str (Izod) @ 23℃ |
48 |
kJ/m² |
ISO 180/1U |
|
|
Notched impact strength (Izod) @ 23℃ |
10 |
kJ/m² |
ISO 180/1A |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
DTUL @ 1.8 MPa |
265 |
℃ |
ISO 75-1/-2 |
|
|
Rheo |
Rheological Calculation properties |
Value |
Unit |
Test Standard |
|
Specific heat capacity of melt |
1300 |
J/(kg K) |
Internal |
Processing
Pre Drying
Yes
Drying time (h):3 - 4
Drying temperature (℃):110 - 120