PPS 6450A6 含玻璃矿物填充
FORTRON® 6450A6 SF3001 NATURAL
FORTRON 6450A6 | PPS | Specialty
Description
Fortron 6450A6 is a fiberglass reinforced, mineral filled alloy that exhibits improved wear and sliding properties versus standard Fortron compounds.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1580 |
kg/m³ |
ISO 1183 |
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile stress at break (5mm/min) |
90 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1.5 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
11000 |
MPa |
ISO 178 |
|
|
Flexural strength (23℃) |
130 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
18 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
6 |
kJ/m² |
ISO 179/1eA |
|
|
Notched impact strength (Izod) @ 23℃ |
6 |
kJ/m² |
ISO 180/1A |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
DTUL @ 1.8 MPa |
260 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
200 |
℃ |
ISO 75-1/-2 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3 - 4
Drying temperature (℃):130 - 140