MECHANICAL

Value

Unit

Standard

Tensile Stress,yld,Type I,5 mm/min

1100

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,5 mm/min

1100

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,10 mm/min

1210

kgf/cm²

SABIC-Japan Method

Tensile Strain,yld,Type I,5 mm/min

1.7

%

ASTM D 638

Tensile Strain,brk,Type I,5 mm/min

1.7

%

ASTM D 638

Tensile Strain,brk,Type I,10 mm/min

8

%

SABIC-Japan Method

Tensile Modulus,5 mm/min

113100

kgf/cm²

ASTM D 638

Flexural Stress,yld,1.3 mm/min,50 mm span

1830

kgf/cm²

ASTM D 790

Flexural Modulus,1.3 mm/min,50 mm span

91400

kgf/cm²

ASTM D 790

Tensile Stress,yield,5 mm/min

97

MPa

ISO 527

Tensile Stress,break,5 mm/min

97

MPa

ISO 527

Tensile Strain,yield,5 mm/min

1

%

ISO 527

Tensile Strain,break,5 mm/min

1

%

ISO 527

Tensile Modulus,1 mm/min

10700

MPa

ISO 527

Flexural Stress,yield,2 mm/min

180

MPa

ISO 178

Flexural Modulus,2 mm/min

9180

MPa

ISO 178

IMPACT

Value

Unit

Standard

Izod Impact,unnotched,23℃

80

cm-kgf/cm

ASTM D 4812

Izod Impact,notched,23℃

9

cm-kgf/cm

ASTM D 256

Izod Impact,notched,-30℃

7

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy,23℃

101

cm-kgf

ASTM D 3763

Izod Impact,notched 80*10*4 +23℃

9

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 -30℃

8

kJ/m²

ISO 180/1A

Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm

21

kJ/m²

ISO 179/1eA

THERMAL

Value

Unit

Standard

Vicat Softening Temp,Rate B/50

157

℃

ASTM D 1525

HDT,1.82 MPa,3.2mm,unannealed

192

℃

ASTM D 648

CTE,-40℃ to 40℃,flow

2.03E-05

1/℃

ASTM E 831

CTE,-40℃ to 40℃,xflow

1.02E-04

1/℃

ASTM E 831

CTE,-40℃ to 40℃,flow

2.03E-05

1/℃

ISO 11359-2

CTE,-40℃ to 40℃,xflow

1.02E-04

1/℃

ISO 11359-2

Vicat Softening Temp,Rate B/50

157

℃

ISO 306

Vicat Softening Temp,Rate B/120

157

℃

ISO 306

HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm

209

℃

ISO 75/Bf

HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm

187

℃

ISO 75/Af

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.65

-

ASTM D 792

Mold Shrinkage,flow,3.2 mm(5)

0.4-0.6

%

SABIC Method

Mold Shrinkage,xflow,3.2 mm(5)

0.4-0.8

%

SABIC Method

Melt Flow Rate,250℃/5.0 kgf

40

g/10 min

ASTM D 1238

Density

1.65

g/cm³

ISO 1183

Water Absorption,(23℃/sat)

0.19

%

ISO 62

Moisture Absorption(23℃/50% RH)

0.06

%

ISO 62

Melt Volume Rate,MVR at 220℃/5.0 kg

27

cm³/10 min

ISO 1133

Melt Volume Rate,MVR at 250℃/5.0 kg

27

cm³/10 min

ISO 1133

ELECTRICAL

Value

Unit

Standard

High Voltage Arc Track Rate{PLC}

4

PLC Code

UL 746A

High Ampere Arc Ign,surface{PLC}

0

PLC Code

UL 746A

Comparative Tracking Index(UL){PLC}

3

PLC Code

UL 746A

Dielectric Strength,in oil,3.2 mm

20

kV/mm

IEC 60243-1

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Compliant,94V-0 Flame Class Rating(3)(4)

0.8

mm

UL 94 by SABIC-IP

UL Compliant,94-5VA Rating(3)(4)

2

mm

UL 94 by SABIC-IP

Injection Molding

Value

Unit

Drying Temperature

120

℃

Drying Time

3-4

hrs

Drying Time(Cumulative)

12

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

230-260

℃

Nozzle Temperature

240-260

℃

Front-Zone 3 Temperature

240-260

℃

Middle-Zone 2 Temperature

230-250

℃

Rear-Zone 1 Temperature

220-240

℃

Mold Temperature

60-120

℃

Back Pressure

0.3-0.7

MPa

Screw Speed

20-100

rpm

Shot to Cylinder Size

30-70

%

Vent Depth

0.025-0.038

mm