MECHANICAL

Value

Unit

Standard

Tensile Stress,yld,Type I,5 mm/min

1060

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,5 mm/min

1060

kgf/cm²

ASTM D 638

Tensile Strain,yld,Type I,5 mm/min

2

%

ASTM D 638

Tensile Strain,brk,Type I,5 mm/min

2

%

ASTM D 638

Tensile Modulus,5 mm/min

112100

kgf/cm²

ASTM D 638

Flexural Stress,yld,1.3 mm/min,50 mm span

1600

kgf/cm²

ASTM D 790

Flexural Modulus,1.3 mm/min,50 mm span

95500

kgf/cm²

ASTM D 790

Tensile Stress,yield,5 mm/min

105

MPa

ISO 527

Tensile Stress,break,5 mm/min

105

MPa

ISO 527

Tensile Strain,yield,5 mm/min

2

%

ISO 527

Tensile Strain,break,5 mm/min

2

%

ISO 527

Tensile Modulus,1 mm/min

10420

MPa

ISO 527

Flexural Stress,yield,2 mm/min

160

MPa

ISO 178

Flexural Stress,break,2 mm/min

160

MPa

ISO 178

Flexural Modulus,2 mm/min

9350

MPa

ISO 178

IMPACT

Value

Unit

Standard

Izod Impact,notched,23℃

4

cm-kgf/cm

ASTM D 256

Izod Impact,notched,-30℃

4

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy,23℃

66

cm-kgf

ASTM D 3763

Izod Impact,unnotched 80*10*4 +23℃

35

kJ/m²

ISO 180/1U

Izod Impact,unnotched 80*10*4 -30℃

32

kJ/m²

ISO 180/1U

Izod Impact,notched 80*10*4 +23℃

6

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 -30℃

5

kJ/m²

ISO 180/1A

Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm

5

kJ/m²

ISO 179/1eA

THERMAL

Value

Unit

Standard

Vicat Softening Temp,Rate B/50

200

℃

ASTM D 1525

HDT,1.82 MPa,3.2mm,unannealed

190

℃

ASTM D 648

CTE,-40℃ to 150℃,flow

2.3E-05

1/℃

ASTM E 831

CTE,-40℃ to 150℃,xflow

7.8E-05

1/℃

ASTM E 831

CTE,-30℃ to 80℃,flow

2.8E-05

1/℃

ISO 11359-2

CTE,-30℃ to 80℃,xflow

1.05E-04

1/℃

ISO 11359-2

Ball Pressure Test,125℃ +/- 2℃

PASSES

-

IEC 60695-10-2

Vicat Softening Temp,Rate B/50

200

℃

ISO 306

Vicat Softening Temp,Rate B/120

200

℃

ISO 306

HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm

190

℃

ISO 75/Af

Relative Temp Index,Elec

130

℃

UL 746B

Relative Temp Index,Mech w/impact

140

℃

UL 746B

Relative Temp Index,Mech w/o impact

140

℃

UL 746B

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.53

-

ASTM D 792

Mold Shrinkage,flow,3.2 mm(5)

0.4-0.9

%

SABIC Method

Mold Shrinkage,xflow,3.2 mm(5)

0.8-1.3

%

SABIC Method

Melt Flow Rate,250℃/5.0 kgf

20

g/10 min

ASTM D 1238

Density

1.52

g/cm³

ISO 1183

Water Absorption,(23℃/sat)

0.25

%

ISO 62

Moisture Absorption(23℃/50% RH)

0.07

%

ISO 62

Melt Volume Rate,MVR at 250℃/5.0 kg

15

cm³/10 min

ISO 1133

ELECTRICAL

Value

Unit

Standard

Hot Wire Ignition{PLC)

0

PLC Code

UL 746A

High Ampere Arc Ign,surface{PLC}

0

PLC Code

UL 746A

Comparative Tracking Index(UL){PLC}

2

PLC Code

UL 746A

Comparative Tracking Index

275

V

IEC 60112

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Recognized,94V-0 Flame Class Rating(3)

0.8

mm

UL 94

UL Recognized,94-5VA Rating(3)

3

mm

UL 94

Glow Wire Flammability Index 960℃,passes at

0.8

mm

IEC 60695-2-12

Glow Wire Ignitability Temperature,3.0 mm

800

℃

IEC 60695-2-13

Injection Molding

Value

Unit

Drying Temperature

110-120

℃

Drying Time

2-4

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

245-260

℃

Nozzle Temperature

230-255

℃

Front-Zone 3 Temperature

240-260

℃

Middle-Zone 2 Temperature

235-250

℃

Rear-Zone 1 Temperature

230-240

℃

Hopper Temperature

40-60

℃

Mold Temperature

40-100

℃