PBT IQ3001 Resin 弹性体改性,抗冲击
VALOX™ PBT IQ3001 Resin
非增强PBT
聚对苯二甲酸丁酯
SABIC Innovative Plastics (Europe-Africa-Middle East)
产品说明
Valox IQ3001 is an unfilled environmentally responsible iQ-PBT resin modified with elastomer. Targeted for flexible hinge applications.
材料特点：弹性体改性,抗冲击
材料用途：针对柔性铰链的应用
定属记号：PBT
塑料牌号：PBT IQ3001
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,yld,Type I,50 mm/min |
570 |
kgf/cm² |
ASTM D 638 |
|
Tensile Stress,brk,Type I,50 mm/min |
520 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain,yld,Type I,50 mm/min |
5 |
% |
ASTM D 638 |
|
Tensile Strain,brk,Type I,50 mm/min |
60 |
% |
ASTM D 638 |
|
Tensile Modulus,5 mm/min |
26500 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress,yld,1.3 mm/min,50 mm span |
830 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus,1.3 mm/min,50 mm span |
25400 |
kgf/cm² |
ASTM D 790 |
|
Tensile Stress,yield,50 mm/min |
55 |
MPa |
ISO 527 |
|
Tensile Stress,break,50 mm/min |
50 |
MPa |
ISO 527 |
|
Tensile Strain,yield,50 mm/min |
5 |
% |
ISO 527 |
|
Tensile Strain,break,50 mm/min |
60 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
2600 |
MPa |
ISO 527 |
|
Flexural Stress,yield,2 mm/min |
80 |
MPa |
ISO 178 |
|
Flexural Modulus,2 mm/min |
2400 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched,23℃ |
173 |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact,notched,23℃ |
2 |
cm-kgf/cm |
ASTM D 256 |
|
Izod Impact,notched,-30℃ |
2 |
cm-kgf/cm |
ASTM D 256 |
|
Instrumented Impact Total Energy,23℃ |
234 |
cm-kgf |
ASTM D 3763 |
|
Izod Impact,notched 80*10*4 +23℃ |
4 |
kJ/m² |
ISO 180/1A |
|
Izod Impact,notched 80*10*4 -30℃ |
4 |
kJ/m² |
ISO 180/1A |
|
Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm |
11 |
kJ/m² |
ISO 179/1eA |
|
THERMAL |
Value |
Unit |
Standard |
|
Vicat Softening Temp,Rate B/50 |
177 |
℃ |
ASTM D 1525 |
|
HDT,1.82 MPa,3.2mm,unannealed |
54 |
℃ |
ASTM D 648 |
|
HDT,0.45 MPa,6.4 mm,unannealed |
148 |
℃ |
ASTM D 648 |
|
CTE,-40℃ to 150℃,flow |
8.5E-05 |
1/℃ |
ASTM E 831 |
|
CTE,-40℃ to 150℃,xflow |
7.9E-05 |
1/℃ |
ASTM E 831 |
|
CTE,-30℃ to 80℃,flow |
8.5E-05 |
1/℃ |
ISO 11359-2 |
|
CTE,-30℃ to 80℃,xflow |
7.9E-05 |
1/℃ |
ISO 11359-2 |
|
Vicat Softening Temp,Rate B/50 |
178 |
℃ |
ISO 306 |
|
Vicat Softening Temp,Rate B/120 |
177 |
℃ |
ISO 306 |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
135 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
48 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Specific Gravity |
1.31 |
- |
ASTM D 792 |
|
Mold Shrinkage,flow,3.2 mm(5) |
2.1-2.7 |
% |
SABIC Method |
|
Mold Shrinkage,xflow,3.2 mm(5) |
2.1-2.7 |
% |
SABIC Method |
|
Melt Flow Rate,250℃/1.2 kgf |
26 |
g/10 min |
ASTM D 1238 |
|
Density |
1.31 |
g/cm³ |
ISO 1183 |
|
Water Absorption,(23℃/sat) |
0.11 |
% |
ISO 62 |
|
Moisture Absorption(23℃/50% RH) |
0.07 |
% |
ISO 62 |
|
Melt Volume Rate,MVR at 250℃/1.2 kg |
24 |
cm³/10 min |
ISO 1133 |
|
FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
|
Glow Wire Ignitability Temperature,1.0 mm |
0 |
℃ |
IEC 60695-2-13 |
|
Glow Wire Ignitability Temperature,2.0 mm |
0 |
℃ |
IEC 60695-2-13 |
|
Glow Wire Ignitability Temperature,3.0 mm |
0 |
℃ |
IEC 60695-2-13 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
120 |
℃ |
|
|
Drying Time |
3-4 |
hrs |
|
|
Drying Time(Cumulative) |
12 |
hrs |
|
|
Maximum Moisture Content |
0.02 |
% |
|
|
Melt Temperature |
250-265 |
℃ |
|
|
Nozzle Temperature |
245-260 |
℃ |
|
|
Front-Zone 3 Temperature |
250-265 |
℃ |
|
|
Middle-Zone 2 Temperature |
245-260 |
℃ |
|
|
Rear-Zone 1 Temperature |
240-255 |
℃ |
|
|
Mold Temperature |
65-90 |
℃ |
|
|
Back Pressure |
0.3-0.7 |
MPa |
|
|
Screw Speed |
50-80 |
rpm |
|
|
Shot to Cylinder Size |
40-80 |
% |
|
|
Vent Depth |
0.025-0.038 |
mm |
|
PBT VALOX™ RESIN
Semi-crystalline polybutylene terephthalate, one of the most widely-used engineering materials, shows low moisture and thermal expansion and offers outstanding wear and friction properties. With good strength at high temperatures, it has good electrical properties and flame resistance.