POM C 13031 XF 耐油
HOSTAFORM® C 13031 XF 10/9022
HOSTAFORM® C 13031 XF 10/9022 BLACK
HOSTAFORM® C 13031 XF 50/5339
HOSTAFORM® C 13031 XF 50/5339 YELLOW
HOSTAFORM C 13031 XF | POM | Specialty
Description
Hostaform® acetal copolymer grade C13031 XF is an acetal copolymer modified to resist deterioration from aggressive fuel blends. This material is specially targeted for transportation industry fuel systems. In natural form, Hostaform® C13031 XF has a distinctive yellow color (Color code 50/5339) to denote use for fuel systems. Additionally the product is available in black 10/9022 for laser welding applications.
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
Melt temperature：190-230℃
Mould temperature：80-120℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1420 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
12 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
2.2 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.9 |
% |
ISO 294-4 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2850 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
62 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
11 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
30 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
2900 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
150 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
140 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
7.5 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
6 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
170 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
102 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 0.45 MPa |
159 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.9 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.9 |
E-4/℃ |
ISO 11359-2 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988-2 |
- |
Internal |
Processing
Pre Drying
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
Drying time (h)：3
Drying temperature (℃)：80 - 100