POM C 13031 抗溶解,耐碱,耐水解
HOSTAFORM® C 13031 10/1570
HOSTAFORM® C 13031 10/2013
HOSTAFORM® C 13031 10/9022
HOSTAFORM® C 13031 10/9022 BLACK
HOSTAFORM® C 13031 11
HOSTAFORM® C 13031 14
HOSTAFORM® C 13031 14 BLACK
HOSTAFORM® C 13031 22
HOSTAFORM® C 13031 30/5693
HOSTAFORM® C 13031 30/5707
HOSTAFORM® C 13031 30/5905
HOSTAFORM® C 13031 33
HOSTAFORM® C 13031 70/5687 LIME GREEN
HOSTAFORM® C 13031 76
HOSTAFORM® C 13031 80/5453
HOSTAFORM® C 13031 80/5688 BLUE
HOSTAFORM® C 13031 87
HOSTAFORM® C 13031 90/5840
HOSTAFORM® C 13031 LS NATURAL
HOSTAFORM® C 13031 NATUR NATURAL
HOSTAFORM® C 13031 NATURAL
HOSTAFORM® C 13031 XAP® NATURAL
HOSTAFORM® C 2520 XAP® LS 40/4112
HOSTAFORM® C 2520 XAP® LS 40/5819
HOSTAFORM C 13031 | POM | Unfilled
Description
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 04-002
POM copolymer
Easy flowing Injection molding type like C 13021, but with higher strength, rigidity and hardness over the entire permissible temperature range for HOSTAFORM; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation.
Fulfils EG-directive 2002/72/EU as well as the recommendation XXXIII for consumer goods of the BgVV, FDA compliant according to 21 CFR 177.2470
UL-registration for all colours and a thickness more than 1.5 mm as UL 94 HB; burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm.
Ranges of applications: For molded parts with higher requirements to strength, rigidity und hardness, ranges of applications with fuel contact.
FDA = Food and Drug Administration (USA)
BgVV = Bundesinstitut fr gesundheitlichen Verbraucherschutz und
Veterin rmedizin
UL = Underwriters Laboratories (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
Melt temperature：190-230℃
Mould temperature：80-120℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1410 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
12 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
2 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.8 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.65 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
3050 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
68 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
8 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
20 |
% |
ISO 527-2/1A |
|
|
Tensile creep modulus (1h) |
2750 |
MPa |
ISO 899-1 |
|
|
Tensile creep modulus (1000h) |
1450 |
MPa |
ISO 899-1 |
|
|
Flexural modulus (23℃) |
3000 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
120 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
120 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
6.7 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
6 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
170 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
107 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.1 |
E-4/℃ |
ISO 11359-2 |
|
|
Flammability @1.6mm nom. thickn. |
HB |
class |
UL94 |
|
|
thickness tested (1.6) |
1.5 |
mm |
UL94 |
|
|
UL recognition (1.6) |
UL |
- |
UL94 |
|
|
Flammability at thickness h |
HB |
class |
UL94 |
|
|
thickness tested (h) |
3 |
mm |
UL94 |
|
|
UL recognition (h) |
UL |
- |
UL94 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 100 Hz |
4 |
- |
IEC 60250 |
|
|
Relative permittivity - 1 MHz |
4 |
- |
IEC 60250 |
|
|
Dissipation factor - 100 Hz |
20 |
E-4 |
IEC 60250 |
|
|
Dissipation factor - 1 MHz |
50 |
E-4 |
IEC 60250 |
|
|
Volume resistivity |
1E12 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
1E14 |
Ohm |
IEC 60093 |
|
|
Electric strength |
35 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
600 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988 |
- |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
The product can then be stored in standard conditions until processed.
Drying time (h)：3 - 4
Drying temperature (℃)：120 - 140