POM C 13031 XAP 低挥发,抗溶解,耐化学
HOSTAFORM C 13031 XAP | POM | Unfilled
Description
Polyacetal copolymer, reduced emission
Easy flowing Injection molding type like C 13021 XAP, but with higher strength, rigidity and hardness over the entire permissible temperature range for HOSTAFORM; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation.
Emissions according to VDA 275 < 10 ppm (natural and colored grades)
Fulfils EG-directive 2002/72/EU as well as the recommendation XXXIII for consumer goods of the BgVV, FDA compliant according to 21 CFR 177.2470 Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm.
Ranges of applications: For molded parts with higher requirements to strength, rigidity und hardness, ranges of applications with fuel contact.
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1410 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
12 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
2 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.8 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.65 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
3050 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
68 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
8 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
20 |
% |
ISO 527-2/1A |
|
|
Tensile creep modulus (1h) |
2750 |
MPa |
ISO 899-1 |
|
|
Tensile creep modulus (1000h) |
1450 |
MPa |
ISO 899-1 |
|
|
Flexural modulus (23℃) |
3000 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
120 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
120 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
6.7 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
6 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
170 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
107 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.1 |
E-4/℃ |
ISO 11359-2 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 100 Hz |
4 |
- |
IEC 60250 |
|
|
Relative permittivity - 1 MHz |
4 |
- |
IEC 60250 |
|
|
Dissipation factor - 100 Hz |
20 |
E-4 |
IEC 60250 |
|
|
Dissipation factor - 1 MHz |
50 |
E-4 |
IEC 60250 |
|
|
Volume resistivity |
1E12 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
1E14 |
Ohm |
IEC 60093 |
|
|
Electric strength |
35 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
600 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988 |
- |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
The product can then be stored in standard conditions until processed.
Drying time (h)：3 - 4
Drying temperature (℃)：120 - 140