佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA66 41 NT 高抗撞击,耐低温冲击,电气/电子应用领域 汽车领域的应用
Vydyne® PA66 41 NT
PA66
聚酰胺66
Ascend Performance Materials Operations LLC
产品说明:
Vydyne 41 NT is a general-purpose, impact-modified PA66 resin. Available in natural, it is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. Vydyne 41 NT is designed to meet the critical low-temperature impact requirements called out in many automotive specifications.
黄卡下载：E70062-100757207
含添加剂：冲击改性剂
材料特性：抗溶剂，高抗撞击，易加工，耐磨损，耐低温冲击，耐化学，耐汽油，耐油
材料用途：齿轮，电气/电子应用领域，电器用具，工业应用，紧固件，连接器，汽车领域的应用，消费品应用领域
加工方法：注射成型
产品外观：自然色粒子
塑料牌号：PA66 41 NT
产品物性：
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
密度 |
1.08 |
-- |
g/cm³ |
ISO 1183 |
|
收缩率 |
|
|
|
ISO 294-4 |
|
垂直流动方向:2.00 mm |
1.6 |
-- |
% |
|
|
流动方向:2.00 mm |
1.8 |
-- |
% |
|
|
吸水率 |
|
|
|
ISO 62 |
|
23℃,24 hr |
1.0 |
-- |
% |
|
|
平衡,23℃,50% RH |
2.1 |
-- |
% |
|
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
1860 |
1390 |
MPa |
ISO 527-2 |
|
拉伸应力 |
|
|
|
ISO 527-2 |
|
屈服,23℃ |
50.0 |
35.0 |
MPa |
|
|
断裂,23℃ |
43.0 |
39.0 |
MPa |
|
|
拉伸应变(断裂,23℃) |
50 |
180 |
% |
ISO 527-2 |
|
弯曲模量(23℃) |
1750 |
545 |
MPa |
ISO 178 |
|
弯曲应力(23℃) |
53.0 |
17.0 |
MPa |
ISO 178 |
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
|
ISO 179 |
|
-40℃ |
20 |
25 |
kJ/m² |
|
|
-30℃ |
35 |
25 |
kJ/m² |
|
|
23℃ |
76 |
110 |
kJ/m² |
|
|
简支梁无缺口冲击强度 |
|
|
|
ISO 179 |
|
-30℃ |
无断裂 |
无断裂 |
|
|
|
23℃ |
无断裂 |
无断裂 |
|
|
|
悬壁梁缺口冲击强度 |
|
|
|
ISO 180 |
|
-40℃ |
22 |
25 |
kJ/m² |
|
|
-30℃ |
40 |
29 |
kJ/m² |
|
|
23℃ |
78 |
88 |
kJ/m² |
|
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
|
0.45 MPa,未退火 |
145 |
-- |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
58.0 |
-- |
℃ |
ISO 75-2/A |
|
熔融温度 |
260 |
-- |
℃ |
ISO 11357-3 |
|
线形热膨胀系数 |
|
|
|
ISO 11359-2 |
|
流动:23 到 55℃,2.00 mm |
1.7E-4 |
-- |
cm/cm/℃ |
|
|
横向:23 到 55℃,2.00 mm |
1.5E-4 |
-- |
cm/cm/℃ |
|
|
RTI Elec |
|
|
|
UL 746 |
|
0.750 mm |
125 |
-- |
℃ |
|
|
1.50 mm |
125 |
-- |
℃ |
|
|
3.00 mm |
125 |
-- |
℃ |
|
|
RTI Imp |
|
|
|
UL 746 |
|
0.750 mm |
75.0 |
-- |
℃ |
|
|
1.50 mm |
75.0 |
-- |
℃ |
|
|
3.00 mm |
75.0 |
-- |
℃ |
|
|
RTI |
|
|
|
UL 746 |
|
0.750 mm |
85.0 |
-- |
℃ |
|
|
1.50 mm |
85.0 |
-- |
℃ |
|
|
3.00 mm |
85.0 |
-- |
℃ |
|
|
电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
体积电阻率(0.750 mm) |
1.0E+11 |
-- |
ohm·cm |
IEC 60093 |
|
介电强度(1.00 mm) |
26 |
-- |
kV/mm |
IEC 60243 |
|
耐电弧性(3.00 mm) |
PLC 5 |
-- |
|
ASTM D495 |
|
漏电起痕指数(3.00 mm) |
600 |
-- |
V |
IEC 60112 |
|
高电弧燃烧指数(HAI) |
|
|
|
UL 746 |
|
0.750 mm |
PLC 0 |
-- |
|
|
|
1.50 mm |
PLC 0 |
-- |
|
|
|
3.00 mm |
PLC 0 |
-- |
|
|
|
高电压电弧起痕速率 (HVTR) |
PLC 0 |
-- |
|
UL 746 |
|
热丝引燃 (HWI) |
|
|
|
UL 746 |
|
0.750 mm |
PLC 4 |
-- |
|
|
|
1.50 mm |
PLC 3 |
-- |
|
|
|
3.00 mm |
PLC 3 |
-- |
|
|
|
可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
|
UL 94 |
|
0.750 mm |
HB |
-- |
|
|
|
1.50 mm |
HB |
-- |
|
|
|
3.00 mm |
HB |
-- |
|
|
|
灼热丝易燃指数 |
|
|
|
IEC 60695-2-12 |
|
0.750 mm |
750 |
-- |
℃ |
|
|
1.50 mm |
700 |
-- |
℃ |
|
|
3.00 mm |
700 |
-- |
℃ |
|
|
热灯丝点火温度 |
|
|
|
IEC 60695-2-13 |
|
0.750 mm |
775 |
-- |
℃ |
|
|
1.50 mm |
725 |
-- |
℃ |
|
|
3.00 mm |
725 |
-- |
℃ |
|
|
补充信息 |
干燥 |
调节后的 |
测试方法 |
|
|
Automotive Materials - (thickness d = 1mm) |
+ |
-- |
FMVSS 302 |
|
|
注射 |
干燥 |
单位制 |
||
|
干燥温度 |
80.0 |
℃ |
||
|
干燥时间 |
4.0 |
hr |
||
|
建议的最大回制料比例 |
25 |
% |
||
|
料筒后部温度 |
280 到 310 |
℃ |
||
|
料筒中部温度 |
280 到 310 |
℃ |
||
|
料筒前部温度 |
280 到 310 |
℃ |
||
|
射嘴温度 |
280 到 310 |
℃ |
||
|
加工（熔体）温度 |
285 到 305 |
℃ |
||
|
模具温度 |
65.0 到 95.0 |
℃ |
||