PA66 25WSP 耐气候,高强度 抗溶剂 耐磨损 耐化学性 韧性良好
Vydyne® PA66 25WSP
PA66
聚酰胺66
Ascend Performance Materials Operations LLC
产品说明:
Vydyne 25WSP is a black, weather-resistant injection-molding grade PA66 resin. This resin offers a well-balanced combination of engineering properties characterized by high strength, rigidity, good toughness, high melt point, good surface lubricity and abrasion resistance. Vydyne 25WSP maintains the chemical resistance typical of PA66 to many chemicals, machine and motor oils, solvents and gasoline.
Weather resistance is obtained by incorporating finely divided, well-dispersed carbon black particles in the PA66 matrix. While the presence of carbon black usually increases brittleness, this resin has been formulated to minimize loss of ductility properties such as elongation and Izod impact strength. As a result, parts molded from 25WSP frequently exhibit higher ductility and practical toughness compared with other black, weather-resistant, non-impact-modified PA66 molded parts.
Vydyne 25WSP resin is internally and externally lubricated for improved machine feed and exceptional mold release. Vydyne 25WSP is intended for use in high-productivity applications. In many applications, the molding cycle can be reduced because molded parts may be removed from the cavity at higher temperatures. In difficult molds where parts have a tendency to stick in the cavity, Vydyne 25WSP can reduce or eliminate the need for mold release sprays. Critical molded part dimensions should be checked against specifications before implementing shorter molding cycles on a routine production basis.
Typical Applications/End Uses:
Lubricated for machine feed and mold release, Vydyne 25WSP provides very good flow and easy moldability. Typical applications include cable ties/tie straps, where its combination of easy flow, good ductility and high tensile strength is particularly attractive, and a wide variety of electrical/electronic and miscellaneous applications requiring weather resistance.
黄卡下载：E70062-249063
含添加剂：润滑剂，碳黑
材料特性：刚性高，高强度，抗溶剂，快的成型周期，良好耐磨损，耐化学性良好，耐汽油，耐油，韧性良好，润滑，脱模性能良好
材料用途：电气/电子应用领域
加工方法：注射成型
产品外观：黑色粒子
塑料牌号：PA66 25WSP
产品物性：
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
密度 |
1.14 |
-- |
g/cm3 |
ISO 1183 |
|
收缩率 |
|
|
|
ISO 294-4 |
|
垂直流动方向:23℃,2.00 mm |
1.4 |
-- |
% |
|
|
流动方向:23℃,2.00 mm |
1.6 |
-- |
% |
|
|
吸水率 |
|
|
|
ISO 62 |
|
23℃,24 hr |
1.2 |
-- |
% |
|
|
平衡,23℃,50% RH |
2.4 |
-- |
% |
|
|
室外适用性 |
f1 |
-- |
|
UL 746C |
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
3400 |
1550 |
MPa |
ISO 527-2 |
|
拉伸应力(屈服,23℃) |
83.0 |
77.0 |
MPa |
ISO 527-2 |
|
拉伸应变(屈服,23℃) |
4.5 |
25 |
% |
ISO 527-2 |
|
标称拉伸断裂应变(23℃) |
20 |
60 |
% |
ISO 527-2 |
|
弯曲模量(23℃) |
3100 |
1400 |
MPa |
ISO 178 |
|
弯曲强度(23℃) |
87.0 |
22.0 |
MPa |
ISO 178 |
|
泊松比 |
0.40 |
-- |
|
ISO 527-2 |
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
|
ISO 179/1eA |
|
-30℃ |
4.8 |
-- |
kJ/m2 |
|
|
23℃ |
6.0 |
-- |
kJ/m2 |
|
|
简支梁无缺口冲击强度 |
|
|
|
ISO 179/1eU |
|
-30℃ |
无断裂 |
-- |
|
|
|
23℃ |
无断裂 |
-- |
|
|
|
悬壁梁缺口冲击强度(23℃) |
6.0 |
-- |
kJ/m2 |
ISO 180 |
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
|
0.45 MPa,未退火 |
225 |
-- |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
70.0 |
-- |
℃ |
ISO 75-2/A |
|
熔融温度 |
260 |
-- |
℃ |
ISO 11357-3 |
|
线形热膨胀系数 |
|
|
|
ISO 11359-2 |
|
流动:23 到 55℃,2.00 mm |
1.0E-4 |
-- |
cm/cm/℃ |
|
|
横向:23 到 55℃,2.00 mm |
1.1E-4 |
-- |
cm/cm/℃ |
|
|
RTI Elec |
|
|
|
UL 746 |
|
0.750 mm |
130 |
-- |
℃ |
|
|
1.50 mm |
130 |
-- |
℃ |
|
|
3.00 mm |
130 |
-- |
℃ |
|
|
RTI Imp |
|
|
|
UL 746 |
|
0.750 mm |
85.0 |
-- |
℃ |
|
|
1.50 mm |
85.0 |
-- |
℃ |
|
|
3.00 mm |
85.0 |
-- |
℃ |
|
|
RTI |
|
|
|
UL 746 |
|
0.750 mm |
75.0 |
-- |
℃ |
|
|
1.50 mm |
75.0 |
-- |
℃ |
|
|
3.00 mm |
75.0 |
-- |
℃ |
|
|
电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
介电强度(1.00 mm) |
26 |
-- |
kV/mm |
IEC 60243 |
|
耐电弧性(3.00 mm) |
PLC 5 |
-- |
|
ASTM D495 |
|
漏电起痕指数(3.00 mm) |
600 |
-- |
V |
IEC 60112 |
|
高电弧燃烧指数(HAI) |
|
|
|
UL 746 |
|
0.750 mm |
PLC 0 |
-- |
|
|
|
1.50 mm |
PLC 0 |
-- |
|
|
|
3.00 mm |
PLC 0 |
-- |
|
|
|
高电压电弧起痕速率 (HVTR) |
PLC 0 |
-- |
|
UL 746 |
|
热丝引燃 (HWI) |
|
|
|
UL 746 |
|
0.750 mm |
PLC 4 |
-- |
|
|
|
1.50 mm |
PLC 3 |
-- |
|
|
|
3.00 mm |
PLC 2 |
-- |
|
|
|
可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
|
UL 94 |
|
0.750 mm |
V-2 |
-- |
|
|
|
1.50 mm |
V-2 |
-- |
|
|
|
3.00 mm |
V-2 |
-- |
|
|
|
灼热丝易燃指数 |
|
|
|
IEC 60695-2-12 |
|
0.750 mm |
850 |
-- |
℃ |
|
|
1.50 mm |
875 |
-- |
℃ |
|
|
3.00 mm |
960 |
-- |
℃ |
|
|
热灯丝点火温度 |
|
|
|
IEC 60695-2-13 |
|
0.750 mm |
700 |
-- |
℃ |
|
|
1.50 mm |
700 |
-- |
℃ |
|
|
3.00 mm |
725 |
-- |
℃ |
|
|
极限氧指数 |
23 |
-- |
% |
ISO 4589-2 |
|
注射 |
干燥 |
单位制 |
||
|
干燥温度 |
< 70.0 |
℃ |
||
|
干燥时间 |
1.0 到 3.0 |
hr |
||
|
建议的最大回制料比例 |
50 |
% |
||
|
料筒后部温度 |
260 到 280 |
℃ |
||
|
料筒中部温度 |
270 到 285 |
℃ |
||
|
料筒前部温度 |
280 到 290 |
℃ |
||
|
射嘴温度 |
280 到 300 |
℃ |
||
|
加工（熔体）温度 |
285 到 300 |
℃ |
||
|
模具温度 |
65.0 到 95.0 |
℃ |
||