PA66 RV007ES 含35%长玻璃纤维,热稳定
LNP™ VERTON™ PA66 RV007ES compound
聚酰胺66
35%长玻璃纤维
SABIC Innovative Plastics (Americas)
产品说明
Also known as:LNP™ VERTON™ Compound RF-7007 EM HS
Product reorder name:RV007ES
LNP VERTON* RV007ES is a compound based on Nylon 66 resin containing 35% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, Structural.
增强填料：含35%长玻璃纤维
材料特点：热稳定,易于成型
塑料牌号：PA66 RV007ES
定属记号：尼龙66
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,break |
2080 |
kgf/cm² |
ASTM D 638 |
|
Flexural Modulus |
100700 |
kgf/cm² |
ASTM D 790 |
|
Tensile Stress,break |
214 |
MPa |
ISO 527 |
|
Tensile Strain,break |
2.1 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
11970 |
MPa |
ISO 527 |
|
Flexural Stress |
309 |
MPa |
ISO 178 |
|
Flexural Modulus |
10240 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,notched,23℃ |
28 |
cm-kgf/cm |
ASTM D 256 |
|
Izod Impact,notched 80*10*4 +23℃ |
29 |
kJ/m² |
ISO 180/1A |
|
Izod Impact,notched 80*10*4 -40℃ |
25 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT,1.82 MPa,3.2mm,unannealed |
245 |
℃ |
ASTM D 648 |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
252 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.42 |
g/cm³ |
ASTM D 792 |
|
Moisture Absorption,50% RH,24 hrs |
0.97 |
% |
ASTM D 570 |
|
Density |
1.42 |
g/cm³ |
ISO 1183 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
290-305 |
℃ |
|
|
Front-Zone 3 Temperature |
290-300 |
℃ |
|
|
Middle-Zone 2 Temperature |
290-300 |
℃ |
|
|
Rear-Zone 1 Temperature |
280-295 |
℃ |
|
|
Mold Temperature |
95-110 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.