PA66 RV007E 含35%长玻璃纤维
LNP™ VERTON™ PA66 RV007E compound
聚酰胺66
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle)
产品说明
LNP* Verton* RV007E is a compound based on Nylon 66 resin containing Long Glass Fiber. Added features of this material include: Easy Molding.
Also known as:LNP™ VERTON™ Compound RF-7007 EM
Product reorder name:RV007E
增强填料：含35%长玻璃纤维
材料特点：易于成型
塑料牌号：PA66 RV007E
定属记号：尼龙66
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,break,5 mm/min |
214 |
MPa |
ISO 527 |
|
Tensile Strain,break,5 mm/min |
2.1 |
% |
ISO 527 |
|
Flexural Stress,break,2 mm/min |
309 |
MPa |
ISO 178 |
|
Flexural Modulus,2 mm/min |
10200 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,notched 80*10*4 +23℃ |
29 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
252 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.42 |
g/cm³ |
ISO 1183 |
|
FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
|
Glow Wire Flammability Index 960℃,passes at |
0.75 |
mm |
IEC 60695-2-12 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
290-305 |
℃ |
|
|
Front-Zone 3 Temperature |
290-300 |
℃ |
|
|
Middle-Zone 2 Temperature |
290-300 |
℃ |
|
|
Rear-Zone 1 Temperature |
280-295 |
℃ |
|
|
Mold Temperature |
95-110 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.