佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA66 RV00CEXS 含60%长玻璃纤维
LNP™ VERTON™ PA66 RV00CEXS compound
聚酰胺66
60%长玻璃纤维
SABIC Innovative Plastics (Americas)
产品说明
Also known as:LNP™ VERTON™ Compound RF-700-12 EM
Product reorder name:RV00CEXS
LNP* VERTON* RV00CEXS is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural.
增强填料：含60%长玻璃纤维
材料特点：易于成型
定属记号：尼龙66
塑料牌号：PA66 RV00CEXS
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,brk,Type I,5 mm/min |
2590 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain,brk,Type I,5 mm/min |
1.6 |
% |
ASTM D 638 |
|
Tensile Modulus,50 mm/min |
225100 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress,yld,1.3 mm/min,50 mm span |
4110 |
kgf/cm² |
ASTM D 790 |
|
Flexural Stress,brk,1.3 mm/min,50 mm span |
4100 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus,1.3 mm/min,50 mm span |
184500 |
kgf/cm² |
ASTM D 790 |
|
Tensile Stress,break,5 mm/min |
264 |
MPa |
ISO 527 |
|
Tensile Strain,break,5 mm/min |
1.6 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
21860 |
MPa |
ISO 527 |
|
Flexural Stress |
404 |
MPa |
ISO 178 |
|
Flexural Modulus,2 mm/min |
18740 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched,23℃ |
119 |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact,notched,23℃ |
41 |
cm-kgf/cm |
ASTM D 256 |
|
Multiaxial Impact |
98 |
cm-kgf |
ISO 6603 |
|
Instrumented Impact Total Energy,23℃ |
138 |
cm-kgf |
ASTM D 3763 |
|
Izod Impact,unnotched 80*10*4 +23℃ |
62 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
37 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT,0.45 MPa,3.2 mm,unannealed |
252 |
℃ |
ASTM D 648 |
|
HDT,1.82 MPa,3.2mm,unannealed |
248 |
℃ |
ASTM D 648 |
|
CTE,-30℃ to 30℃,flow |
4.93E+01 |
1/℃ |
ASTM D 696 |
|
CTE,-30℃ to 30℃,xflow |
6.3E+01 |
1/℃ |
ASTM D 696 |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
253 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
247 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Specific Gravity |
1.72 |
- |
ASTM D 792 |
|
Density |
1.72 |
g/cm³ |
ASTM D 792 |
|
Moisture Absorption,50% RH,24 hrs |
0.53 |
% |
ASTM D 570 |
|
Mold Shrinkage,flow,24 hrs (5) |
0.3-0.5 |
% |
ASTM D 955 |
|
Mold Shrinkage,xflow,24 hrs (5) |
0.7-0.9 |
% |
ASTM D 955 |
|
Moisture Absorption (23℃/50% RH) |
0.67 |
% |
ISO 62 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
290-305 |
℃ |
|
|
Front-Zone 3 Temperature |
290-300 |
℃ |
|
|
Middle-Zone 2 Temperature |
290-300 |
℃ |
|
|
Rear-Zone 1 Temperature |
280-295 |
℃ |
|
|
Mold Temperature |
95-110 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.