佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA66 RV00CEXP 含长玻璃纤维
LNP™ VERTON™ PA66 RV00CEXP compound
聚酰胺66
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle)
产品说明
Also known as:LNP™ VERTON™ Compound RF-700-12 EM
Product reorder name:RV00CEXP
LNP* VERTON* RV00CE is a compound based on PA66 resin containing Long Glass Fiber. Added features include; Easy Molding.
增强填料：含长玻璃纤维
材料特点：易于成型
塑料牌号：PA66 RV00CEXP
定属记号：尼龙66
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,break,5 mm/min |
270 |
MPa |
ISO 527 |
|
Tensile Strain,break,5 mm/min |
1.7 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
21600 |
MPa |
ISO 527 |
|
Flexural Stress,break,2 mm/min |
430 |
MPa |
ISO 178 |
|
Flexural Strain,break,2 mm/min |
2.6 |
% |
ISO 178 |
|
Flexural Modulus,2 mm/min |
19000 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched 80*10*4 +23℃ |
100 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
53 |
kJ/m² |
ISO 180/1A |
|
Izod Impact,notched 80*10*4 -40℃ |
43 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
CTE,23℃ to 60℃,flow |
1.7E-05 |
1/℃ |
ISO 11359-2 |
|
CTE,23℃ to 60℃,xflow |
5.3E-05 |
1/℃ |
ISO 11359-2 |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
255 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
252 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Mold Shrinkage,flow(5) |
0.26 |
% |
SABIC Method |
|
Mold Shrinkage,xflow(5) |
0.61 |
% |
SABIC Method |
|
Density |
1.71 |
g/cm³ |
ISO 1183 |
|
Water Absorption,23℃/24hrs |
0.9 |
% |
ISO 62-1 |
|
Moisture Absorption(23℃/50% RH) |
1.1 |
% |
ISO 62 |
|
FLAME CHARACTERISTICS |
Value |
Unit |
Standard |
|
UL Recognized,94HB Flame Class Rating(3) |
0.8 |
mm |
UL 94 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
290-305 |
℃ |
|
|
Front-Zone 3 Temperature |
290-300 |
℃ |
|
|
Middle-Zone 2 Temperature |
290-300 |
℃ |
|
|
Rear-Zone 1 Temperature |
280-295 |
℃ |
|
|
Mold Temperature |
95-110 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.