PPS 1131L4 ITT 含30%玻璃纤维增强
FORTRON 1131L4 ITT | PPS | Glass Reinforced
PPS 1131L4 ITT 是一个含30%玻璃纤维增强的聚苯硫醚材料。
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1560 |
kg/m³ |
ISO 1183 |
|
Mold shrinkage - parallel |
0.3-0.7 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
0.5-0.8 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
12200 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
165 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1.9 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
12000 |
MPa |
ISO 178 |
|
|
Flexural stress @ break |
255 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
42 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
42 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
8 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
8 |
kJ/m² |
ISO 179/1eA |
|
|
Notched impact strength (Izod) @ 23℃ |
8 |
kJ/m² |
ISO 180/1A |
|
|
Notched impact strength (Izod) @-30℃ |
8 |
kJ/m² |
ISO 180/1A |
|
|
Rockwell hardness |
100 |
M-Scale |
ISO 2039-2 |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
280 |
℃ |
ISO 11357-1,-2,-3 |
|
|
Glass transition temperature (10℃/min) |
90 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
265 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
205 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.29 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.62 |
E-4/℃ |
ISO 11359-2 |
|
|
Flammability @1.6mm nom. thickn. |
V-0 |
class |
UL94 |
|
|
thickness tested (1.6) |
1.5 |
mm |
UL94 |
|
|
Flammability at thickness h |
V-0 |
class |
UL94 |
|
|
thickness tested (h) |
0.38 |
mm |
UL94 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Volume resistivity |
>1E13 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
>1E15 |
Ohm |
IEC 60093 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Injection molding melt temperature |
310-340 |
℃ |
ISO 294 |
|
|
Injection molding mold temperature |
135-160 |
℃ |
ISO 294 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3-4
Drying temperature (℃):130-140