FORTRON 1130L4 | PPS | Glass Reinforced
Description
Fortron 1130L4 is a 30% glass-reinforced PPS that has excellent heat and chemical resistance. It is inherently flame-retardant and exhibits high hardness and a good balance of strength and stiffness. Especially used for thin walled parts requiring long flow lengths. This grade also exhibits excellent weldability in secondary operations due to its low filler content.
Other Processing
Injection Molding
On injection molding machines with 15-25 D long three-section screws, as are usual in the trade, the FORTRON is processable. A shut-off nozzle is preferred to a free-flow nozzle.
Melt temperature 320-340 degC
Mold wall temperature at least 140 degC
A medium injection rate is normally preferred. All mold cavities must be effectively vented.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1580 |
kg/m³ |
ISO 1183 |
|
Mold shrinkage - parallel |
0.3-0.5 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
0.6-0.9 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
12000 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
170 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
1.9 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
11000 |
MPa |
ISO 178 |
|
|
Flexural stress @ break |
260 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
34 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
34 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
9 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
9 |
kJ/m² |
ISO 179/1eA |
|
|
Unnotched impact str (Izod) @ 23℃ |
30 |
kJ/m² |
ISO 180/1U |
|
|
Notched impact strength (Izod) @ 23℃ |
9 |
kJ/m² |
ISO 180/1A |
|
|
Notched impact strength (Izod) @-30℃ |
9 |
kJ/m² |
ISO 180/1A |
|
|
Rockwell hardness |
100 |
M-Scale |
ISO 2039-2 |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Glass transition temperature (10℃/min) |
90 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
255 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.29 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
0.52 |
E-4/℃ |
ISO 11359-2 |
|
|
Flammability @1.6mm nom. thickn. |
V-0 |
class |
UL94 |
|
|
thickness tested (1.6) |
1.5 |
mm |
UL94 |
|
|
Flammability at thickness h |
V-0 |
class |
UL94 |
|
|
thickness tested (h) |
0.8 |
mm |
UL94 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Volume resistivity |
>1E13 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
>1E15 |
Ohm |
IEC 60093 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Injection molding melt temperature |
310-340 |
℃ |
ISO 294 |
|
|
Injection molding mold temperature |
135-160 |
℃ |
ISO 294 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3-4
Drying temperature (℃):130-140