佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PPS 1115T1 含15%玻纤增强,吹塑级
FORTRON 1115T1 | PPS | Specialty
Description
Fortron® 1115T1 is a 15% fiberglass-reinforced grade of polyphenylene sulfide suitable for blow molding applications.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1410 |
kg/m³ |
ISO 1183 |
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
6700 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
115 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
2.5 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
6500 |
MPa |
ISO 178 |
|
|
Flexural strength (23℃) |
190 |
MPa |
ISO 178 |
|
|
Flexural strain @ break |
2.9 |
% |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
39 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
6.2 |
kJ/m² |
ISO 179/1eA |
|
|
Unnotched impact str (Izod) @ 23℃ |
34 |
kJ/m² |
ISO 180/1U |
|
|
Notched impact strength (Izod) @ 23℃ |
7 |
kJ/m² |
ISO 180/1A |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
DTUL @ 1.8 MPa |
210 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
104 |
℃ |
ISO 75-1/-2 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3-4
Drying temperature (℃):80-100