FORTRON 1115L0 | PPS | Specialty
Description
Fortron® 1115L0 is a 15% fiberglass-reinforced grade of polyphenylene sulfide with high melt strength suitable for blow molding and extrusion applications.
The recommended processing conditions are similar to those of our standard grades, except drying conditions are somewhat milder at 80 to 100 C for 3-4 hours.
|
ISO Data |
Physical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1440 |
kg/m³ |
ISO 1183 |
|
Water absorption (23℃-sat) |
0.02 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
7700 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at break (5mm/min) |
120 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at break (5mm/min) |
2 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
7500 |
MPa |
ISO 178 |
|
|
Flexural strength (23℃) |
200 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
32 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
5 |
kJ/m² |
ISO 179/1eA |
|
|
Notched impact strength (Izod) @ 23℃ |
5.2 |
kJ/m² |
ISO 180/1A |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
DTUL @ 1.8 MPa |
220 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 8.0 MPa |
115 |
℃ |
ISO 75-1/-2 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Surface resistivity |
>1E15 |
Ohm |
IEC 60093 |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.02%
FORTRON should in principle be predried. Because of the necessary low maximum residual moisture content the use of dry air dryers is recommended. The dew point should be =< - 30℃. The time between drying and processing should be as short as possible.
For subsequent storage the material should be stored dry in the dryer until processed (<= 60 h).
Drying time (h):3-4
Drying temperature (℃):110-120