MECHANICAL

Value

Unit

Standard

Tensile Stress,yld,Type I,5 mm/min

1160

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,5 mm/min

1160

kgf/cm²

ASTM D 638

Tensile Strain,yld,Type I,5 mm/min

2.2

%

ASTM D 638

Tensile Strain,brk,Type I,5 mm/min

2.2

%

ASTM D 638

Tensile Modulus,5 mm/min

120300

kgf/cm²

ASTM D 638

Flexural Stress,yld,1.3 mm/min,50 mm span

2140

kgf/cm²

ASTM D 790

Flexural Stress,brk,1.3 mm/min,50 mm span

1920

kgf/cm²

ASTM D 790

Flexural Modulus,1.3 mm/min,50 mm span

92700

kgf/cm²

ASTM D 790

Tensile Stress,yield,5 mm/min

139

MPa

ISO 527

Tensile Stress,break,5 mm/min

139

MPa

ISO 527

Tensile Strain,yield,5 mm/min

1.6

%

ISO 527

Tensile Strain,break,5 mm/min

1.6

%

ISO 527

Tensile Modulus,1 mm/min

10700

MPa

ISO 527

Flexural Stress,yield,2 mm/min

210

MPa

ISO 178

Flexural Modulus,2 mm/min

9100

MPa

ISO 178

IMPACT

Value

Unit

Standard

Izod Impact,unnotched,23℃

78

cm-kgf/cm

ASTM D 4812

Izod Impact,notched,23℃

8

cm-kgf/cm

ASTM D 256

Izod Impact,notched,-30℃

8

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy,23℃

71

cm-kgf

ASTM D 3763

Izod Impact,notched 80*10*4 +23℃

8

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 -30℃

8

kJ/m²

ISO 180/1A

Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm

14

kJ/m²

ISO 179/1eA

THERMAL

Value

Unit

Standard

Vicat Softening Temp,Rate B/50

206

℃

ASTM D 1525

HDT,1.82 MPa,3.2mm,unannealed

203

℃

ASTM D 648

HDT,1.82 MPa,6.4 mm,unannealed

207

℃

ASTM D 648

CTE,-40℃ to 40℃,flow

2.5E-05

1/℃

ASTM E 831

CTE,-40℃ to 40℃,xflow

8.9E-05

1/℃

ASTM E 831

CTE,-40℃ to 40℃,flow

2.5E-05

1/℃

ISO 11359-2

CTE,-40℃ to 40℃,xflow

8.9E-05

1/℃

ISO 11359-2

Ball Pressure Test,approximate maximum

200

℃

IEC 60695-10-2

Vicat Softening Temp,Rate B/50

206

℃

ISO 306

Vicat Softening Temp,Rate B/120

206

℃

ISO 306

HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm

217

℃

ISO 75/Bf

HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm

205

℃

ISO 75/Af

Relative Temp Index,Elec

140

℃

UL 746B

Relative Temp Index,Mech w/impact

140

℃

UL 746B

Relative Temp Index,Mech w/o impact

140

℃

UL 746B

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.54

-

ASTM D 792

Water Absorption,24 hours

0.1

%

ASTM D 570

Mold Shrinkage,flow,3.2 mm(5)

0.5-0.7

%

SABIC Method

Mold Shrinkage,xflow,3.2 mm(5)

0.8-1

%

SABIC Method

Melt Flow Rate,250℃/5.0 kgf

52

g/10 min

ASTM D 1238

Density

1.54

g/cm³

ISO 1183

Water Absorption,(23℃/sat)

0.09

%

ISO 62

Moisture Absorption(23℃/50% RH)

0.1

%

ISO 62

Melt Volume Rate,MVR at 250℃/5.0 kg

38

cm³/10 min

ISO 1133

ELECTRICAL

Value

Unit

Standard

Volume Resistivity

>1.E+15

Ohm-cm

ASTM D 257

Dielectric Strength,in air,3.2 mm

23

kV/mm

ASTM D 149

High Voltage Arc Track Rate{PLC}

2

PLC Code

UL 746A

Comparative Tracking Index(UL){PLC}

2

PLC Code

UL 746A

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Recognized,94HB Flame Class Rating(3)

0.84

mm

UL 94

Injection Molding

Value

Unit

Drying Temperature

120

℃

Drying Time

3-4

hrs

Drying Time(Cumulative)

12

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

250-265

℃

Nozzle Temperature

245-260

℃

Front-Zone 3 Temperature

250-265

℃

Middle-Zone 2 Temperature

245-260

℃

Rear-Zone 1 Temperature

240-255

℃

Mold Temperature

65-90

℃

Back Pressure

0.3-0.7

MPa

Screw Speed

50-80

rpm

Shot to Cylinder Size

40-80

%

Vent Depth

0.025-0.038

mm