MECHANICAL

Value

Unit

Standard

Tensile Stress,yld,Type I,5 mm/min

1120

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,5 mm/min

1120

kgf/cm²

ASTM D 638

Tensile Strain,yld,Type I,5 mm/min

2

%

ASTM D 638

Tensile Strain,brk,Type I,5 mm/min

2

%

ASTM D 638

Tensile Modulus,5 mm/min

112100

kgf/cm²

ASTM D 638

Flexural Stress,yld,1.3 mm/min,50 mm span

1520

kgf/cm²

ASTM D 790

Flexural Stress,brk,1.3 mm/min,50 mm span

1520

kgf/cm²

ASTM D 790

Flexural Modulus,1.3 mm/min,50 mm span

91700

kgf/cm²

ASTM D 790

Tensile Stress,yield,5 mm/min

105

MPa

ISO 527

Tensile Stress,break,5 mm/min

105

MPa

ISO 527

Tensile Strain,yield,5 mm/min

2

%

ISO 527

Tensile Strain,break,5 mm/min

2

%

ISO 527

Tensile Modulus,1 mm/min

11000

MPa

ISO 527

Flexural Stress,yield,2 mm/min

170

MPa

ISO 178

Flexural Stress,break,2 mm/min

170

MPa

ISO 178

Flexural Strain,break,2 mm/min

2

%

ISO 178

Flexural Modulus,2 mm/min

10000

MPa

ISO 178

Hardness,H358/30

142

MPa

ISO 2039-1

Hardness,Rockwell R

120

-

ISO 2039-2

IMPACT

Value

Unit

Standard

Charpy Impact,unnotched,23℃

40

kJ/m²

ISO 179/2C

Charpy Impact,unnotched,-30℃

35

kJ/m²

ISO 179/2C

Izod Impact,unnotched,23℃

50

cm-kgf/cm

ASTM D 4812

Izod Impact,unnotched,-30℃

50

cm-kgf/cm

ASTM D 4812

Izod Impact,notched,23℃

7

cm-kgf/cm

ASTM D 256

Izod Impact,notched,0℃

7

cm-kgf/cm

ASTM D 256

Izod Impact,notched,-30℃

7

cm-kgf/cm

ASTM D 256

Izod Impact,unnotched 80*10*4 +23℃

37

kJ/m²

ISO 180/1U

Izod Impact,unnotched 80*10*4 -30℃

37

kJ/m²

ISO 180/1U

Izod Impact,notched 80*10*4 +23℃

9

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 0℃

9

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 -30℃

9

kJ/m²

ISO 180/1A

Charpy Impact,notched,23℃

10

kJ/m²

ISO 179/2C

Charpy Impact,notched,-30℃

10

kJ/m²

ISO 179/2C

THERMAL

Value

Unit

Standard

Vicat Softening Temp,Rate A/50

217

℃

ASTM D 1525

Vicat Softening Temp,Rate B/50

207

℃

ASTM D 1525

HDT,0.45 MPa,3.2 mm,unannealed

223

℃

ASTM D 648

HDT,1.82 MPa,3.2mm,unannealed

210

℃

ASTM D 648

CTE,-40℃ to 40℃,flow

2.E-05

1/℃

ISO 11359-2

CTE,-40℃ to 40℃,xflow

6.2E-05

1/℃

ISO 11359-2

CTE,23℃ to 150℃,flow

2.5E-05

1/℃

ISO 11359-2

CTE,23℃ to 150℃,xflow

1.5E-04

1/℃

ISO 11359-2

Ball Pressure Test,125℃ +/- 2℃

PASSES

-

IEC 60695-10-2

Vicat Softening Temp,Rate A/50

220

℃

ISO 306

Vicat Softening Temp,Rate B/50

206

℃

ISO 306

Vicat Softening Temp,Rate B/120

205

℃

ISO 306

HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm

225

℃

ISO 75/Bf

HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm

210

℃

ISO 75/Af

Relative Temp Index,Elec

140

℃

UL 746B

Relative Temp Index,Mech w/impact

125

℃

UL 746B

Relative Temp Index,Mech w/o impact

140

℃

UL 746B

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.56

-

ASTM D 792

Filler Content

30

%

ASTM D 229

Melt Flow Rate,265℃/5.0 kgf

23

g/10 min

ASTM D 1238

Density

1.56

g/cm³

ISO 1183

Melt Volume Rate,MVR at 250℃/5.0 kg

16

cm³/10 min

ISO 1133

Melt Viscosity,260℃,1500 sec-1

110

Pa-s

ISO 11443

ELECTRICAL

Value

Unit

Standard

Volume Resistivity

1.E+14

Ohm-cm

ASTM D 257

Dielectric Strength,in oil,0.8 mm

32

kV/mm

ASTM D 149

Dielectric Strength,in oil,1.6 mm

22

kV/mm

ASTM D 149

Dielectric Strength,in oil,3.2 mm

18

kV/mm

ASTM D 149

Relative Permittivity,1 MHz

3.8

-

ASTM D 150

Dissipation Factor,1 MHz

0.14

-

ASTM D 150

Hot Wire Ignition{PLC)

0

PLC Code

UL 746A

High Ampere Arc Ign,surface{PLC}

0

PLC Code

UL 746A

Comparative Tracking Index(UL){PLC}

0

PLC Code

UL 746A

Volume Resistivity

1.E+14

Ohm-cm

IEC 60093

Surface Resistivity,ROA

>1.E+15

Ohm

IEC 60093

Dielectric Strength,in oil,0.8 mm

32

kV/mm

IEC 60243-1

Dielectric Strength,in oil,1.6 mm

22

kV/mm

IEC 60243-1

Dielectric Strength,in oil,3.2 mm

18

kV/mm

IEC 60243-1

Relative Permittivity,1 MHz

3.8

-

IEC 60250

Dissipation Factor,1 MHz

0.14

-

IEC 60250

Comparative Tracking Index

600

V

IEC 60112

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Recognized,94V-0 Flame Class Rating(3)

0.8

mm

UL 94

UL Recognized,94-5VB Rating(3)

3

mm

UL 94

Glow Wire Flammability Index 960℃,passes at

1-3

mm

IEC 60695-2-12

Glow Wire Ignitability Temperature,1.0 mm

750

℃

IEC 60695-2-13

Glow Wire Ignitability Temperature,2.0 mm

750

℃

IEC 60695-2-13

Glow Wire Ignitability Temperature,3.0 mm

800

℃

IEC 60695-2-13

Injection Molding

Value

Unit

Drying Temperature

110-120

℃

Drying Time

2-4

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

245-260

℃

Nozzle Temperature

230-255

℃

Front-Zone 3 Temperature

240-260

℃

Middle-Zone 2 Temperature

235-250

℃

Rear-Zone 1 Temperature

230-240

℃

Hopper Temperature

40-60

℃

Mold Temperature

40-100

℃