MECHANICAL

Value

Unit

Standard

Tensile Stress,yld,Type I,5 mm/min

1170

kgf/cm²

ASTM D 638

Tensile Stress,brk,Type I,5 mm/min

1170

kgf/cm²

ASTM D 638

Tensile Strain,yld,Type I,5 mm/min

2

%

ASTM D 638

Tensile Strain,brk,Type I,5 mm/min

2

%

ASTM D 638

Tensile Modulus,5 mm/min

105000

kgf/cm²

ASTM D 638

Flexural Stress,yld,1.3 mm/min,50 mm span

1680

kgf/cm²

ASTM D 790

Flexural Stress,brk,1.3 mm/min,50 mm span

1680

kgf/cm²

ASTM D 790

Flexural Modulus,1.3 mm/min,50 mm span

86600

kgf/cm²

ASTM D 790

Tensile Stress,yield,5 mm/min

112

MPa

ISO 527

Tensile Stress,break,5 mm/min

112

MPa

ISO 527

Tensile Strain,yield,5 mm/min

2

%

ISO 527

Tensile Strain,break,5 mm/min

2

%

ISO 527

Tensile Modulus,1 mm/min

10400

MPa

ISO 527

Flexural Stress,yield,2 mm/min

175

MPa

ISO 178

Flexural Stress,break,2 mm/min

175

MPa

ISO 178

Flexural Strain,break,2 mm/min

2

%

ISO 178

Flexural Modulus,2 mm/min

9200

MPa

ISO 178

Hardness,H358/30

174

MPa

ISO 2039-1

Hardness,Rockwell R

124

-

ISO 2039-2

IMPACT

Value

Unit

Standard

Charpy Impact,unnotched,23℃

45

kJ/m²

ISO 179/2C

Charpy Impact,unnotched,-30℃

40

kJ/m²

ISO 179/2C

Izod Impact,unnotched,23℃

56

cm-kgf/cm

ASTM D 4812

Izod Impact,unnotched,-30℃

56

cm-kgf/cm

ASTM D 4812

Izod Impact,notched,23℃

7

cm-kgf/cm

ASTM D 256

Izod Impact,notched,0℃

7

cm-kgf/cm

ASTM D 256

Izod Impact,notched,-30℃

7

cm-kgf/cm

ASTM D 256

Instrumented Impact Total Energy,23℃

66

cm-kgf

ASTM D 3763

Izod Impact,unnotched 80*10*4 +23℃

40

kJ/m²

ISO 180/1U

Izod Impact,unnotched 80*10*4 -30℃

38

kJ/m²

ISO 180/1U

Izod Impact,notched 80*10*4 +23℃

8

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 0℃

8

kJ/m²

ISO 180/1A

Izod Impact,notched 80*10*4 -30℃

8

kJ/m²

ISO 180/1A

Charpy 23℃,V-notch Edgew 80*10*4 sp=62mm

5

kJ/m²

ISO 179/1eA

Charpy Impact,notched,23℃

9

kJ/m²

ISO 179/2C

Charpy Impact,notched,-30℃

9

kJ/m²

ISO 179/2C

THERMAL

Value

Unit

Standard

Vicat Softening Temp,Rate A/50

215

℃

ASTM D 1525

Vicat Softening Temp,Rate B/50

205

℃

ASTM D 1525

HDT,0.45 MPa,3.2 mm,unannealed

220

℃

ASTM D 648

HDT,1.82 MPa,3.2mm,unannealed

205

℃

ASTM D 648

CTE,-40℃ to 40℃,flow

2.3E-05

1/℃

ASTM E 831

CTE,-40℃ to 40℃,xflow

5.9E-05

1/℃

ASTM E 831

CTE,-40℃ to 40℃,flow

2.7E-05

1/℃

ISO 11359-2

CTE,-40℃ to 40℃,xflow

7.1E-05

1/℃

ISO 11359-2

CTE,23℃ to 80℃,flow

2.2E-05

1/℃

ISO 11359-2

CTE,23℃ to 80℃,xflow

9.1E-05

1/℃

ISO 11359-2

CTE,23℃ to 150℃,flow

2.5E-05

1/℃

ISO 11359-2

CTE,23℃ to 150℃,xflow

1.48E-04

1/℃

ISO 11359-2

Ball Pressure Test,125℃ +/- 2℃

Pass

-

IEC 60695-10-2

Vicat Softening Temp,Rate A/50

220

℃

ISO 306

Vicat Softening Temp,Rate B/50

208

℃

ISO 306

Vicat Softening Temp,Rate B/120

207

℃

ISO 306

HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm

220

℃

ISO 75/Bf

HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm

210

℃

ISO 75/Af

Relative Temp Index,Elec

130

℃

UL 746B

Relative Temp Index,Mech w/impact

140

℃

UL 746B

Relative Temp Index,Mech w/o impact

140

℃

UL 746B

PHYSICAL

Value

Unit

Standard

Specific Gravity

1.52

-

ASTM D 792

Filler Content

25

%

ASTM D 229

Water Immersion,Start F1 from 1mm onword

0

-

UL 746C

UV Weathering,Start F1 from 1mm onword

0

-

UL 746C

Mold Shrinkage on Tensile Bar,flow(2)(5)

0.1-0.5

%

SABIC Method

Mold Shrinkage,flow,3.2 mm(5)

0.1-0.5

%

SABIC Method

Mold Shrinkage on Tensile Bar,xflow(2)(5)

0.6-1.2

%

SABIC Method

Mold Shrinkage,xflow,3.2 mm(5)

0.5-1.1

%

SABIC Method

Melt Flow Rate,250℃/5.0 kgf

27

g/10 min

ASTM D 1238

Melt Flow Rate,265℃/5.0 kgf

25

g/10 min

ASTM D 1238

Density

1.52

g/cm³

ISO 1183

Water Absorption,(23℃/sat)

0.23

%

ISO 62

Moisture Absorption(23℃/50% RH)

0.06

%

ISO 62

Melt Volume Rate,MVR at 250℃/5.0 kg

20

cm³/10 min

ISO 1133

Melt Volume Rate,MVR at 265℃/5.0 kg

17

cm³/10 min

ISO 1133

Melt Viscosity,250℃,1500 sec-1

210

Pa-s

ISO 11443

Melt Viscosity,260℃,1500 sec-1

160

Pa-s

ISO 11443

ELECTRICAL

Value

Unit

Standard

Volume Resistivity

1.E+15

Ohm-cm

ASTM D 257

Dielectric Strength,in air,3.2 mm

21

kV/mm

ASTM D 149

Dielectric Strength,in oil,0.8 mm

30

kV/mm

ASTM D 149

Dielectric Strength,in oil,1.6 mm

24

kV/mm

ASTM D 149

Dielectric Strength,in oil,3.2 mm

19

kV/mm

ASTM D 149

Relative Permittivity,1 MHz

3.4

-

ASTM D 150

Dissipation Factor,1 MHz

0.12

-

ASTM D 150

Arc Resistance,Tungsten{PLC}

6

PLC Code

ASTM D 495

Hot Wire Ignition{PLC)

0

PLC Code

UL 746A

High Voltage Arc Track Rate{PLC}

0

PLC Code

UL 746A

High Ampere Arc Ign,surface{PLC}

0

PLC Code

UL 746A

Comparative Tracking Index(UL){PLC}

2

PLC Code

UL 746A

Volume Resistivity

1.E+15

Ohm-cm

IEC 60093

Surface Resistivity,ROA

>1.E+15

Ohm

IEC 60093

Dielectric Strength,in oil,0.8 mm

30

kV/mm

IEC 60243-1

Dielectric Strength,in oil,1.6 mm

24

kV/mm

IEC 60243-1

Dielectric Strength,in oil,3.2 mm

19

kV/mm

IEC 60243-1

Relative Permittivity,1 MHz

3.4

-

IEC 60250

Dissipation Factor,1 MHz

0.12

-

IEC 60250

Comparative Tracking Index

300

V

IEC 60112

FLAME CHARACTERISTICS

Value

Unit

Standard

UL Recognized,94V-0 Flame Class Rating(3)

0.3

mm

UL 94

UL Recognized,94-5VA Rating(3)

2

mm

UL 94

Oxygen Index(LOI)

34

%

ASTM D 2863

Glow Wire Flammability Index 960℃,passes at

0.4

mm

IEC 60695-2-12

Glow Wire Ignitability Temperature,0.4 mm

775

℃

IEC 60695-2-13

Glow Wire Ignitability Temperature,0.8 mm

775

℃

IEC 60695-2-13

Glow Wire Ignitability Temperature,3.0 mm

775

℃

IEC 60695-2-13

Glow Wire Ignitability Temperature,3.0 mm,by VDE

775

℃

IEC 60695-2-13

Injection Molding

Value

Unit

Drying Temperature

110-120

℃

Drying Time

2-4

hrs

Maximum Moisture Content

0.02

%

Melt Temperature

245-260

℃

Nozzle Temperature

230-255

℃

Front-Zone 3 Temperature

240-260

℃

Middle-Zone 2 Temperature

235-250

℃

Rear-Zone 1 Temperature

230-240

℃

Hopper Temperature

40-60

℃

Mold Temperature

40-100

℃