POM S 9362 XAP 低挥发,抗撞击性良好
HOSTAFORM® S 9362 XAP2™ NATURAL
HOSTAFORM S 9362 XAP² ™ | POM | Impact Modified
Description
Preliminary Data Sheet
Hostaform® acetal copolymer grade S 9362 XAP2 ™ is an impact modified grade for applications requiring improved impact. Hostaform® S 9362 XAP2 ™ provides good impact strength while improving modulus and weld line strength over standard impact modified grades such as Hostaform® S 9063, and also exhibits exceptional low emission performance meeting or exceeding the requirements of many automotive markets.
Chemical abbreviation according to ISO 1043-1: POM-HI
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1390 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
6.5 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
1.9 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.8 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.8 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2300 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
55 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
10 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
2200 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
NB |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
190 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
10 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
6 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
166 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
87 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 0.45 MPa |
151 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.1 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
1.1 |
E-4/℃ |
ISO 11359-2 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988-2 |
- |
Internal |
Processing
Pre Drying
Drying is suggested to help achieve low emission performance and to counter if material has contacted moisture through improper storage and handling.
Drying time (h):3
Drying temperature (℃):80 - 100