POM MR130HPB 高刚性,韧性良好
HOSTAFORM® MR130HPB 14 BLACK
HOSTAFORM® MR130HPB NATURAL
HOSTAFORM MR130HPB | POM | Specialty
Description
Preliminary Data Sheet
Hostaform® MR130HPB acetal copolymer is a high modulus, improved toughness grade based on our Hostaform® C 13031 product but specially formulated with improved resistance to intermittent bleach exposure.
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
Melt temperature：190-230℃
Mould temperature：80-120℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1410 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
13 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Water absorption (23℃-sat) |
0.8 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
3100 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
69 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
9 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
3000 |
MPa |
ISO 178 |
|
|
Charpy notched impact strength @ 23℃ |
6.5 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
6 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
170 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
107 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.2 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
1.2 |
E-4/℃ |
ISO 11359-2 |
Processing
Pre Drying
Drying not normally required. If material has contacted moisture through improper storage, handling, or regrind use, drying may be needed to prevent splay and odor.
The product can then be stored in standard conditions until processed.
Drying time (h)：3 - 4
Drying temperature (℃)：100 - 120