HOSTAFORM MR130ACS | POM | Specialty
Description
Hostaform® acetal copolymer grade MR130ACS is a general purpose acetal with improved acid stabilization. Hostaform® MR130ACS demonstrates improved performance over standard acetals after intermittent exposure to acidic cleaners.
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
Melt temperature：190-230℃
Mould temperature：80-120℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1410 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
12 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Water absorption (23℃-sat) |
1.7 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2900 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
62 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
11 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
30 |
% |
ISO 527-2/1A |
|
|
Charpy impact strength @ 23℃ |
150 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
140 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
8 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
6 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
170 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
100 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.94 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
1 |
E-4/℃ |
ISO 11359-2 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988-2 |
- |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
Standard drying conditions are 82 deg C (180 deg F) for 3 hours.
Drying time (h)：3 - 4
Drying temperature (℃)：120 - 140