POM LX90Z 抗紫外线良好
HOSTAFORM® LX90Z CC44477 SATIN CHROME
HOSTAFORM® LX90Z CC44704 MED SPECKLE MET
HOSTAFORM® LX90Z CC44750 OBSIDIAN 9PC
HOSTAFORM® LX90Z CC44751 DK SLATE METAL
HOSTAFORM® LX90Z CC44753 LIQUID CHROME
HOSTAFORM® LX90Z CC44759 BRIGHT CHROME
HOSTAFORM® LX90Z CC44761 MED SATIN NICKE
HOSTAFORM® LX90Z CC44762 BRITE NICKEL 6Q
HOSTAFORM® LX90Z CC44766 SATIN PEWTER 8P
HOSTAFORM® LX90Z CC44768 DK GRANITE META
HOSTAFORM® LX90Z CC44792 LT WARM STEEL 7
HOSTAFORM® LX90Z CC44869 DK SILVER FOUND
HOSTAFORM® LX90Z CC44881 SILVER
HOSTAFORM® LX90Z CC44936 POLISHED PEWTER
HOSTAFORM LX90Z | POM | UV Resistant
Description
Hostaform® LX90Z specialty metallic appearance grades are an integrally colored nominal 9 melt flow rate based acetal copolymer material stabilized for use where ultraviolet radiation exposure is to be encountered. The material is formulated to prevent discoloration, fading, chalking and mechanical property change in severe ultraviolet exposure.
This product, formerly called Celcon® UV90Z metallics, is available in many molded-in-color metallic colors formulated for the interior automotive market and other applications.
Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Ticona Technical Service for assistance with your application.
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1430 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
8 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
2.3 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.4 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.75 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2800 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
54 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
10 |
% |
ISO 527-2/1A |
|
|
Flexural modulus (23℃) |
2850 |
MPa |
ISO 178 |
|
|
Charpy notched impact strength @ 23℃ |
4 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
4 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
166 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
88 |
℃ |
ISO 75-1/-2 |
|
|
DTUL @ 0.45 MPa |
151 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
0.9 |
E-4/℃ |
ISO 11359-2 |
|
|
Coeff.of linear therm. expansion (normal) |
1 |
E-4/℃ |
ISO 11359-2 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988-2 |
- |
Internal |
Processing
Pre Drying
Drying is required for this material to prevent poor appearance and performance of the part.
Drying time (h)：3
Drying temperature (℃)：105 - 110