POM C 9021 10/1570 含碳黑,耐化学,耐油
HOSTAFORM® C 9021 10/1570 BLACK
HOSTAFORM C 9021 10/1570 | POM | Specialty
Description
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GCL, 03-002
POM copolymer
Standard Injection molding type, UV-stabilized with carbon black; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation.
UL-registration for a thickness more than 1.5 mm as UL 94 HB, temperature index UL 746 B electrical 110℃, mechanical 90℃.
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm.
Ranges of applications: exterior applications.
UL = Underwriters Laboratories (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
Melt temperature:190-230℃
Mould temperature:80-120℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1420 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
8 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
2 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.8 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.65 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
3000 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
64 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
8 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
25 |
% |
ISO 527-2/1A |
|
|
Tensile creep modulus (1h) |
2500 |
MPa |
ISO 899-1 |
|
|
Tensile creep modulus (1000h) |
1400 |
MPa |
ISO 899-1 |
|
|
Charpy impact strength @ 23℃ |
110 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
110 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
6.5 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
6 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
167 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
105 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.1 |
E-4/℃ |
ISO 11359-2 |
|
|
Flammability @1.6mm nom. thickn. |
HB |
class |
UL94 |
|
|
thickness tested (1.6) |
1.5 |
mm |
UL94 |
|
|
UL recognition (1.6) |
UL |
- |
UL94 |
|
|
Flammability at thickness h |
HB |
class |
UL94 |
|
|
thickness tested (h) |
3 |
mm |
UL94 |
|
|
UL recognition (h) |
UL |
- |
UL94 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Volume resistivity |
1E12 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
1E14 |
Ohm |
IEC 60093 |
|
|
Electric strength |
28 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
300 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988 |
- |
Internal |