POM C 2521 高抗撞击,耐水解,耐化学
HOSTAFORM® C 2521
HOSTAFORM® C 2521 10/1570
HOSTAFORM® C 2521 10/5358
HOSTAFORM® C 2521 10/9022
HOSTAFORM® C 2521 14 BLACK
HOSTAFORM® C 2521 20/1922
HOSTAFORM® C 2521 20/1922 L
HOSTAFORM® C 2521 20/5690
HOSTAFORM® C 2521 22
HOSTAFORM® C 2521 30/3753
HOSTAFORM® C 2521 30/5633 L
HOSTAFORM® C 2521 39
HOSTAFORM® C 2521 40/2365 L
HOSTAFORM® C 2521 40/5379 L
HOSTAFORM® C 2521 46
HOSTAFORM® C 2521 50/2401
HOSTAFORM® C 2521 50/2761
HOSTAFORM® C 2521 50/2762
HOSTAFORM® C 2521 60/5672 L
HOSTAFORM® C 2521 80/3726
HOSTAFORM® C 2521 80/3726 L
HOSTAFORM® C 2521 80/5498 L
HOSTAFORM® C 2521 80/6119
HOSTAFORM® C 2521 87
HOSTAFORM® C 2521 95400
HOSTAFORM® C 2521 FAI 80/0918
HOSTAFORM® C 2521 LS
HOSTAFORM® C 2521 LS 40/5295
HOSTAFORM® C 2521 LS 40/5782
HOSTAFORM® C 2521 LS 40/6188
HOSTAFORM® C 2521 LS 50/5692
HOSTAFORM® C 2521 LS 80/5824
HOSTAFORM® C 2521 LS 90/0259
HOSTAFORM® C 2521 LS NATURAL
HOSTAFORM® C 2521 NATURAL
HOSTAFORM® C 2521 XAP®
HOSTAFORM® C 2521 XAP® 14 BLACK
HOSTAFORM® C 2521 XAP® LS 14 BLACK
HOSTAFORM C 2521 | POM | Unfilled
Description
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 01-002
POM copolymer
Stiff-flowing type for injection molding and extrusion with high impact toughness and good tracking resistance over a high range of temperature; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation.
Fulfils EG-directive 2002/72/EU as well as the recommendation XXXIII for consumer goods of the BgVV FDA compliant according to 21 CFR 177.2470
Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm.
Ranges of applications: injection molding thick-walled, void-free molded parts; extrusion e.g. for boards and pipes.
FDA = Food and Drug Administration (USA)
BgVV = Bundesinstitut fr gesundheitlichen Verbraucherschutz und
Veterin rmedizin
FMVSS = Federal Motor Vehicle Safety Standard (USA)
Other Processing
Injection Molding
Standard injection moulding machines with three phase (15 to 25 D) plasticating screws will fit.
Melt temperature：190-230℃
Mould temperature：80-120℃
Film Extrusion
Standard extruders with grooved feed zone and short compression screws (minimum 25 D) will fit.
Melt temperature：180-190℃
Other Extrusion
Standard extruders with grooved feed zone and short compression screws (minimum 25 D) will fit.
Melt temperature：180-190℃
Profile Extrusion
Standard extruders with grooved feed zone and short compression screws (minimum 25 D) will fit.
Melt temperature：180-190℃
Sheet Extrusion
Standard extruders with grooved feed zone and short compression screws (minimum 25 D) will fit.
Melt temperature：180-190℃
Blow Molding
Standard extruders with plasticating screws (20 to 25 D) will fit.
Melt temperature：180-190℃
Mould-surface temperature：60-100℃
|
ISO Data |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Phys |
Density |
1410 |
kg/m³ |
ISO 1183 |
|
Melt volume rate (MVR) |
2.5 |
cm³/10min |
ISO 1133 |
|
|
MVR test temperature |
190 |
℃ |
ISO 1133 |
|
|
MVR test load |
2.16 |
kg |
ISO 1133 |
|
|
Mold shrinkage - parallel |
2.1 |
% |
ISO 294-4 |
|
|
Mold shrinkage - normal |
1.8 |
% |
ISO 294-4 |
|
|
Water absorption (23℃-sat) |
0.65 |
% |
ISO 62 |
|
|
Mech |
Mechanical properties |
Value |
Unit |
Test Standard |
|
Tensile modulus (1mm/min) |
2600 |
MPa |
ISO 527-2/1A |
|
|
Tensile stress at yield (50mm/min) |
62 |
MPa |
ISO 527-2/1A |
|
|
Tensile strain at yield (50mm/min) |
9 |
% |
ISO 527-2/1A |
|
|
Nominal strain at break (50mm/min) |
32 |
% |
ISO 527-2/1A |
|
|
Tensile creep modulus (1h) |
2300 |
MPa |
ISO 899-1 |
|
|
Tensile creep modulus (1000h) |
1100 |
MPa |
ISO 899-1 |
|
|
Flexural modulus (23℃) |
2500 |
MPa |
ISO 178 |
|
|
Charpy impact strength @ 23℃ |
220P |
kJ/m² |
ISO 179/1eU |
|
|
Charpy impact strength @ -30℃ |
200 |
kJ/m² |
ISO 179/1eU |
|
|
Charpy notched impact strength @ 23℃ |
8.5 |
kJ/m² |
ISO 179/1eA |
|
|
Charpy notched impact strength @ -30℃ |
7 |
kJ/m² |
ISO 179/1eA |
|
|
Therm |
Thermal properties |
Value |
Unit |
Test Standard |
|
Melting temperature (10℃/min) |
165 |
℃ |
ISO 11357-1,-2,-3 |
|
|
DTUL @ 1.8 MPa |
101 |
℃ |
ISO 75-1/-2 |
|
|
Coeff.of linear therm. expansion (parallel) |
1.1 |
E-4/℃ |
ISO 11359-2 |
|
|
Flammability @1.6mm nom. thickn. |
HB |
class |
UL94 |
|
|
thickness tested (1.6) |
1.5 |
mm |
UL94 |
|
|
UL recognition (1.6) |
UL |
- |
UL94 |
|
|
Flammability at thickness h |
HB |
class |
UL94 |
|
|
thickness tested (h) |
3 |
mm |
UL94 |
|
|
UL recognition (h) |
UL |
- |
UL94 |
|
|
Elec |
Electrical properties |
Value |
Unit |
Test Standard |
|
Relative permittivity - 100 Hz |
4 |
- |
IEC 60250 |
|
|
Relative permittivity - 1 MHz |
4 |
- |
IEC 60250 |
|
|
Dissipation factor - 100 Hz |
15 |
E-4 |
IEC 60250 |
|
|
Dissipation factor - 1 MHz |
50 |
E-4 |
IEC 60250 |
|
|
Volume resistivity |
1E12 |
Ohm*m |
IEC 60093 |
|
|
Surface resistivity |
1E14 |
Ohm |
IEC 60093 |
|
|
Electric strength |
35 |
kV/mm |
IEC 60243-1 |
|
|
Comparative tracking index CTI |
600 |
- |
IEC 60112 |
|
|
SpecProd |
Test specimen production |
Value |
Unit |
Test Standard |
|
Processing conditions acc. ISO |
9988 |
- |
Internal |
|
|
Rheo |
Rheological Calculation properties |
Value |
Unit |
Test Standard |
|
Density of melt |
1200 |
kg/m³ |
Internal |
|
|
Thermal conductivity of melt |
0.155 |
W/(m K) |
Internal |
|
|
Specific heat capacity of melt |
2210 |
J/(kg K) |
Internal |
|
|
Ejection temperature |
165 |
℃ |
Internal |
Processing
Pre Drying
Necessary low maximum residual moisture content: 0.15%
Drying is not normally required. If material has come in contact with moisture through improper storage or handling or through regrind use, drying may be necessary to prevent splay and odor problems.
The product can then be stored in standard conditions until processed.
Drying time (h)：3 - 4
Drying temperature (℃)：120 - 140