PA6 SEGM35 H1 BK6259 含40%玻璃/矿物填充,汽车领域的应用
Ultramid® PA6 SEGM35 H1 BK6259
聚酰胺6
玻璃/矿物,40%
BASF Corporation
产品说明
Ultramid SEGM35 H1 BK6259 is a 40% glass/mineral reinforced injection molding grade. It offers enhanced surface appearance, it also exhibits similar UV weathering characteristics compared to 8267G HS BK-106. In parts containing cross sections, significant pressure drops are encountered during filling.
Ultramid SEGM35 H1 BK6259 is generally recommended for applications such as mirror housings, rear liftgate handles and luggage rack components.
填料增强：含40%玻璃/矿物填充
材料特点：外观良好
材料用途：把手，汽车领域的应用
外观颜色：黑色
产品形式：颗粒料
加工方法：注射成型
塑料牌号：PA6 SEGM35 H1 BK6259
定属记号：尼龙6
物料数据
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
密度 |
1.48 |
g/cm3 |
ISO 1183 |
|
溶化体积流率(MVR)(235℃/5.0kg) |
27 |
cm3/10min |
ISO 1133 |
|
吸水率 |
|
|
ISO 62 |
|
23℃,24 hr |
0.90 |
% |
|
|
饱和,23℃ |
5.7 |
% |
|
|
平衡,23℃,50% RH |
1.6 |
% |
|
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸应力(断裂,23℃) |
80 |
MPa |
ISO 527-2 |
|
弯曲模量(23℃) |
4800 |
MPa |
ISO 178 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度(23℃) |
2.4 |
kJ/m2 |
ISO 180 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度(1.8 MPa,未退火) |
144 |
℃ |
ISO 75-2/A |
|
溶融温度(DSC) |
220 |
℃ |
ISO 3146 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
80.0 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.1 |
% |
|
|
加工(熔体)温度 |
270 到 295 |
℃ |
|
|
模具温度 |
80.0 到 95.0 |
℃ |
|
|
注塑温度 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
- |
|
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.