PA6 SEGM35 H1 BK-126 含15%玻纤增强和含25%矿物填料
Ultramid® PA6 SEGM35 H1 BK-126
聚酰胺6
玻璃纤维增强材料,15%;矿物填料,25%
BASF Corporation
产品说明
Ultramid SEGM35 H1 BK-126 is a 40% glass/mineral reinforced injection molding grade. It offers enhanced surface appearance, it also exhibits similar UV weathering characteristics compared to 8267G HS BK-106. In parts containing cross sections, significant pressure drops are encountered during filling.
Applications
Ultramid SEGM35 H1 BK-126 is generally recommended for applications such as mirror housings, rear liftgate handles and luggage rack components.
含添加剂：热稳定剂
填料增强：含15%玻璃纤维增强材料和含25%矿物填料
材料特点：尺寸稳定，低粘度，刚性佳，抗紫外线，易加工，表面光洁度好，抗热老化，流动性好，耐化学，耐磨蚀
材料用途：Electrical Housing，把手，工业领域，汽车领域的应用，汽车外部零件，外壳
外观颜色：黑色
产品形式：颗粒料
加工方法：注射成型
塑料牌号：PA6 SEGM35 H1 BK-126
定属记号：尼龙6
物料数据
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
比重 |
1.48 |
-- |
g/cm3 |
ASTM D792,ISO 1183 |
|
收缩率 - 流动(3.18 mm) |
0.40 |
-- |
% |
|
|
吸水率 |
|
|
|
|
|
24 hr |
0.90 |
-- |
% |
ASTM D570 |
|
23℃,24 hr |
0.90 |
-- |
% |
ISO 62 |
|
饱和 |
5.7 |
-- |
% |
ASTM D570 |
|
饱和,23℃ |
5.7 |
-- |
% |
ISO 62 |
|
平衡,50% RH |
1.6 |
-- |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
1.6 |
-- |
% |
ISO 62 |
|
硬度 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
洛氏硬度(R 级) |
121 |
-- |
|
ASTM D785 |
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
|
ISO 527-2 |
|
-40℃ |
9210 |
-- |
MPa |
|
|
23℃ |
8290 |
3900 |
MPa |
|
|
80℃ |
3310 |
3050 |
MPa |
|
|
121℃ |
2760 |
2320 |
MPa |
|
|
抗张强度 |
|
|
|
|
|
断裂,-40℃ |
175 |
153 |
MPa |
ASTM D638,ISO 527-2 |
|
断裂,23℃ |
119 |
-- |
MPa |
ASTM D638 |
|
断裂,80℃ |
58.0 |
46.0 |
MPa |
ASTM D638,ISO 527-2 |
|
断裂,121℃ |
49.0 |
38.0 |
MPa |
ASTM D638,ISO 527-2 |
|
断裂,23℃ |
119 |
67.0 |
MPa |
ISO 527-2 |
|
伸长率 |
|
|
|
|
|
断裂,-40℃ |
2.9 |
2.6 |
% |
ASTM D638 |
|
断裂,23℃ |
2.6 |
-- |
% |
ASTM D638 |
|
断裂,80℃ |
6.6 |
5.9 |
% |
ASTM D638 |
|
断裂,121℃ |
7.6 |
7.3 |
% |
ASTM D638 |
|
断裂,23℃ |
2.6 |
5.6 |
% |
ISO 527-2 |
|
弯曲模量 |
|
|
|
|
|
23℃ |
7600 |
-- |
MPa |
ASTM D790 |
|
23℃ |
7000 |
-- |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
|
23℃ |
200 |
-- |
MPa |
ASTM D790 |
|
23℃ |
186 |
-- |
MPa |
ISO 178 |
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度(23℃) |
4.0 |
-- |
kJ/m2 |
ISO 179 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
|
23℃ |
53 |
-- |
J/m |
ASTM D256 |
|
-40℃ |
4.3 |
-- |
kJ/m2 |
ISO 180 |
|
23℃ |
5.8 |
-- |
kJ/m2 |
ISO 180 |
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
|
0.45 MPa,未退火 |
215 |
-- |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
190 |
-- |
℃ |
ASTM D648,ISO 75-2/A |
|
熔融峰值温度 |
220 |
-- |
℃ |
ASTM D3418,ISO 3146 |
|
注射 |
干燥 |
单位制 |
||
|
干燥温度 |
83.0 |
℃ |
||
|
干燥时间 |
2.0 到 4.0 |
hr |
||
|
建议的最大水分含量 |
0.15 |
% |
||
|
加工（熔体）温度 |
270 到 295 |
℃ |
||
|
模具温度 |
80.0 到 95.0 |
℃ |
||
|
注塑压力 |
3.50 到 12.5 |
MPa |
||
|
注射速度 |
快速 |
|
||
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.