PA6 8234G HS BK-102 含44%玻纤增强,热稳定,尺寸稳定 高强度 高耐热
Ultramid® PA6 8234G HS BK-102
聚酰胺6
玻璃纤维增强材料,44%
BASF Corporation
产品说明
Ultramid 8234G HS BK-102 is heat stabilized, pigmented black, 44% glass reinforced PA6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensional stability. Its resistance to creep under load is excellent. It maintains its inherent chemical resistance to greases, oils and hydrocarbons. It is available in natural and black versions. Pigmented and weatherable versions may be offered on a case by case basis.
Ultramid 8234G HS BK-102 is generally recommended for applications such as consumer power tool housings, cattle ear taggers, luggage frames, fans and pressure regulator housings.
黄卡下载：E36632-231132
含添加剂：热稳定剂
填料增强：含44%玻璃纤维增强材料
材料特点：尺寸稳定，刚性高，高强度，抗蠕变，耐化学，耐磨蚀，高耐热，耐碳氢化合物，耐油脂，热稳定性
材料用途：动力/其它工具，皮箱，外壳
外观颜色：黑色
外观形式：颗粒料
加工方法：注射成型
塑料牌号：PA6 8234G HS BK-102
定属记号：尼龙6
物料数据
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
比重 |
1.49 |
-- |
g/cm3 |
ASTM D792,ISO 1183 |
|
收缩率 - 流动(3.18 mm) |
0.20 |
-- |
% |
|
|
吸水率 |
|
|
|
|
|
24 hr |
0.90 |
-- |
% |
ASTM D570 |
|
23℃,24 hr |
0.90 |
-- |
% |
ISO 62 |
|
饱和 |
5.2 |
-- |
% |
ASTM D570 |
|
饱和,23℃ |
5.2 |
-- |
% |
ISO 62 |
|
平衡,50% RH |
1.5 |
-- |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
1.5 |
-- |
% |
ISO 62 |
|
硬度 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
洛氏硬度(R 级) |
121 |
-- |
|
ASTM D785 |
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
抗张强度 |
|
|
|
|
|
断裂,23℃ |
193 |
145 |
MPa |
ASTM D638 |
|
断裂,23℃ |
195 |
-- |
MPa |
ISO 527-2 |
|
伸长率 |
|
|
|
|
|
断裂,23℃ |
2.0 |
6.0 |
% |
ASTM D638 |
|
断裂,23℃ |
2.0 |
-- |
% |
ISO 527-2 |
|
弯曲模量 |
|
|
|
|
|
-40℃ |
12300 |
14700 |
MPa |
ASTM D790 |
|
23℃ |
11700 |
6560 |
MPa |
ASTM D790 |
|
65℃ |
7000 |
-- |
MPa |
ASTM D790 |
|
121℃ |
4830 |
-- |
MPa |
ASTM D790 |
|
23℃ |
11800 |
-- |
MPa |
ISO 178 |
|
弯曲强度 |
|
|
|
|
|
-40℃ |
450 |
410 |
MPa |
ASTM D790 |
|
23℃ |
352 |
212 |
MPa |
ASTM D790 |
|
65℃ |
220 |
-- |
MPa |
ASTM D790 |
|
90℃ |
160 |
-- |
MPa |
ASTM D790 |
|
121℃ |
138 |
-- |
MPa |
ASTM D790 |
|
23℃ |
290 |
-- |
MPa |
ISO 178 |
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度(23℃) |
15 |
-- |
kJ/m2 |
ISO 179 |
|
简支梁无缺口冲击强度(23℃) |
70 |
-- |
kJ/m2 |
ISO 179 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
|
23℃ |
130 |
-- |
J/m |
ASTM D256 |
|
23℃ |
14 |
-- |
kJ/m2 |
ISO 180 |
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
|
0.45 MPa,未退火 |
220 |
-- |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
210 |
-- |
℃ |
ASTM D648,ISO 75-2/A |
|
熔融峰值温度 |
220 |
-- |
℃ |
ASTM D3418,ISO 3146 |
|
线形热膨胀系数 - 流动 |
3.1E-5 |
-- |
cm/cm/℃ |
ASTM E831 |
|
RTI Elec |
|
|
|
UL 746 |
|
0.710 mm |
130 |
-- |
℃ |
|
|
1.50 mm |
140 |
-- |
℃ |
|
|
3.00 mm |
140 |
-- |
℃ |
|
|
RTI Imp |
|
|
|
UL 746 |
|
0.710 mm |
95.0 |
-- |
℃ |
|
|
1.50 mm |
105 |
-- |
℃ |
|
|
3.00 mm |
105 |
-- |
℃ |
|
|
RTI |
|
|
|
UL 746 |
|
0.710 mm |
130 |
-- |
℃ |
|
|
1.50 mm |
140 |
-- |
℃ |
|
|
3.00 mm |
140 |
-- |
℃ |
|
|
可燃性 |
干燥 |
调节后的 |
|
测试方法 |
|
UL 阻燃等级 |
|
|
|
UL 94 |
|
1.50 mm |
HB |
-- |
|
|
|
3.00 mm |
HB |
-- |
|
|
|
补充信息 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
Drop Weight Impact Strength(23℃) |
3.25 |
-- |
J |
内部方法 |
|
注射 |
干燥 |
单位制 |
||
|
干燥温度 |
80.0 |
℃ |
||
|
干燥时间 |
2.0 到 4.0 |
hr |
||
|
建议的最大水分含量 |
0.060 |
% |
||
|
加工（熔体）温度 |
280 到 305 |
℃ |
||
|
模具温度 |
80.0 到 95.0 |
℃ |
||
|
注塑压力 |
3.50 到 12.5 |
MPa |
||
|
注射速度 |
快速 |
|
||
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.