佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA6 PX06419 compound 含专有填料,热稳定
LNP™ VERTON™ PA6 PX06419 compound
聚酰胺6
专有填料
SABIC Innovative Plastics (Americas)
产品说明
LNP* VERTON* PX06419 is a compound based on Nylon 6 resin containing Proprietary Filler(s). Added features of this material include: Heat Stabilized, Structural.
Also known as:LNP™ VERTON™ Compound PDX-P-00783 HS
Product reorder name:PX06419
增强填料：含专有填料
材料特点：热稳定
塑料牌号：PA6 PX06419
定属记号：尼龙6
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,break |
2330 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain,break |
2.2 |
% |
ASTM D 638 |
|
Tensile Modulus,50 mm/min |
177800 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress |
3020 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus |
155300 |
kgf/cm² |
ASTM D 790 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched,23℃ |
163 |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact,notched,23℃ |
36 |
cm-kgf/cm |
ASTM D 256 |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT,1.82 MPa,3.2mm,unannealed |
205 |
℃ |
ASTM D 648 |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.61 |
g/cm³ |
ASTM D 792 |
|
Mold Shrinkage,flow,24 hrs(5) |
0.2 |
% |
ASTM D 955 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
265-275 |
℃ |
|
|
Front-Zone 3 Temperature |
275-290 |
℃ |
|
|
Middle-Zone 2 Temperature |
265-275 |
℃ |
|
|
Rear-Zone 1 Temperature |
250-260 |
℃ |
|
|
Mold Temperature |
80-95 |
℃ |
|
|
Back Pressure |
0.3-0.7 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA6 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6 is among the most-used engineering materials, with excellent impact strength, moldability and paintability, fair heat resistance, and good wear and friction characteristics.