佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA6 PX06418 compound 含专有填料,热稳定
LNP™ VERTON™ PA6 PX06418 compound
聚酰胺6
专有填料
SABIC Innovative Plastics (Americas)
产品说明
LNP* VERTON* PX06418 is a compound based on Nylon 6 containing proprietary fillers. Added features of this grade are: Heat Stabilized, Structural.
Also known as:LNP™ VERTON™ Compound PDX-P-00700 HS
Product reorder name:PX06418
增强填料：含专有填料
材料特点：热稳定
塑料牌号：PA6 PX06418
定属记号：尼龙6
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,brk,Type I,5 mm/min |
2060 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain,brk,Type I,5 mm/min |
2.5 |
% |
ASTM D 638 |
|
Tensile Modulus,50 mm/min |
121900 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress,yld,1.3 mm/min,50 mm span |
3150 |
kgf/cm² |
ASTM D 790 |
|
Flexural Stress,brk,1.3 mm/min,50 mm span |
3130 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus,1.3 mm/min,50 mm span |
101900 |
kgf/cm² |
ASTM D 790 |
|
Tensile Stress,yield,5 mm/min |
193 |
MPa |
ISO 527 |
|
Tensile Stress,break,5 mm/min |
182 |
MPa |
ISO 527 |
|
Tensile Strain,break,5 mm/min |
2.6 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
10900 |
MPa |
ISO 527 |
|
Flexural Stress |
290 |
MPa |
ISO 178 |
|
Flexural Modulus,2 mm/min |
9530 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched,23℃ |
106 |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact,notched,23℃ |
28 |
cm-kgf/cm |
ASTM D 256 |
|
Multiaxial Impact |
53 |
cm-kgf |
ISO 6603 |
|
Instrumented Impact Total Energy,23℃ |
156 |
cm-kgf |
ASTM D 3763 |
|
Izod Impact,unnotched 80*10*4 +23℃ |
64 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
27 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT,0.45 MPa,3.2 mm,unannealed |
213 |
℃ |
ASTM D 648 |
|
HDT,1.82 MPa,3.2mm,unannealed |
208 |
℃ |
ASTM D 648 |
|
CTE,-30℃ to 30℃,flow |
4.77E+01 |
1/℃ |
ASTM D 696 |
|
CTE,-30℃ to 30℃,xflow |
1.14E+02 |
1/℃ |
ASTM D 696 |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
213 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
207 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Specific Gravity |
1.41 |
- |
ASTM D 792 |
|
Density |
1.4 |
g/cm³ |
ASTM D 792 |
|
Moisture Absorption,50% RH,24 hrs |
1.1 |
% |
ASTM D 570 |
|
Mold Shrinkage,flow,24 hrs(5) |
0.1-0.3 |
% |
ASTM D 955 |
|
Mold Shrinkage,xflow,24 hrs(5) |
0.4-0.6 |
% |
ASTM D 955 |
|
Moisture Absorption(23℃/50% RH) |
1.7 |
% |
ISO 62 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
265-275 |
℃ |
|
|
Front-Zone 3 Temperature |
275-290 |
℃ |
|
|
Middle-Zone 2 Temperature |
265-275 |
℃ |
|
|
Rear-Zone 1 Temperature |
250-260 |
℃ |
|
|
Mold Temperature |
80-95 |
℃ |
|
|
Back Pressure |
0.3-0.7 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA6 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6 is among the most-used engineering materials, with excellent impact strength, moldability and paintability, fair heat resistance, and good wear and friction characteristics.