佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA6 SEG8 GY7716B 加40%玻纤增强,冲击改性,韧性良好
Ultramid® SEG8 GY7716B
40%玻璃纤维增强材料
聚酰胺6
BASF Corporation
产品说明:
Ultramid SEG8 GY7716B is a 40% glass reinforced, impact modified, injection molding type 6 nylon requiring high strength, surface aesthetics, improved UV resistance, and good processability. This product has excellent surface appearance while maintaining a good balance of physical properties, such as high strength, improved toughness and chemical resistance. It features superior flow properties and is suited for gas assist parts and those requiring long lengths. It shows lower pressure, temperature and cycle time requirements than conventional grades.
Applications
Applications may include furniture, lawn and garden, and universal, but can be used wherever strength and appearance are critical requirements. Additionally, with improved UV performance, the use of this material in exterior applications may be applicable.
含添加剂：冲击改性剂
填料增强：含40%玻璃纤维增强
材料特性：冲击改性，高强度，可加工性良好，流动性高，耐化学，韧性良好，外观良好
材料用途：草坪和园林设备，家具，通用
加工方法：注射成型
塑料牌号：PA6 SEG8 GY7716B
产品物性：
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
密度 |
1.43 |
g/cm³ |
ISO 1183 |
|
溶化体积流率(MVR)(235℃/5.0 kg) |
6.00 |
cm³/10min |
ISO 1133 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸应力(断裂,23℃) |
130 |
MPa |
ISO 527-2 |
|
拉伸应变(断裂,23℃) |
2.0 |
% |
ISO 527-2 |
|
弯曲模量(23℃) |
10500 |
MPa |
ISO 178 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度(23℃) |
11 |
kJ/m² |
ISO 179 |
|
悬壁梁缺口冲击强度(23℃) |
13 |
kJ/m² |
ISO 180 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度(1.8 MPa,未退火) |
200 |
℃ |
ISO 75-2/A |
|
溶融温度（DSC） |
220 |
℃ |
ISO 3146 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
80.0 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.080 |
% |
|
|
料筒后部温度 |
245 到 275 |
℃ |
|
|
料筒中部温度 |
260 到 285 |
℃ |
|
|
料筒前部温度 |
270 到 295 |
℃ |
|
|
射嘴温度 |
270 到 295 |
℃ |
|
|
加工（熔体）温度 |
270 到 295 |
℃ |
|
|
模具温度 |
80.0 到 95.0 |
℃ |
|
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
|
|
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.