PA66 R860 BK02 含玻纤和矿物填充,高强度 润滑
Vydyne® R860 BK02
玻璃纤维增强材料;矿物填料
聚酰胺66
Ascend Performance Materials Operations LLC
产品说明:
Vydyne R860 BK02 is general-purpose, glass-fiber and mineral-reinforced PA66 resin. Available in black, this product is also lubricated for improved flow and offers superior surface appearance.
Glass fiber and mineral-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Typical Applications/End Uses:
Vydyne R860 BK02 can be successfully used in a wide range of injection-molding engineering applications. Typical parts include automotive clips, radiator shrouds, fans and mirror brackets; electrical connectors, housings and bobbins; and industrial applications such as gears, bearing shells, covers and housings.
填料增强：含玻璃纤维增强和矿物填料
含添加剂：润滑剂
材料特性：出色的外观，高刚性，高拉伸强度，高强度，润滑，脱模性能良好
材料用途：草坪和园林设备，齿轮，动力/其它工具，金属取代，外壳，汽车的发动机罩下的零件
加工方法：注射成型
产品外观：黑色粒子
塑料牌号：PA66 R860 BK02
产品物性：
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
密度 |
1.47 |
-- |
g/cm³ |
ISO 1183 |
|
收缩率 |
|
|
|
ISO 294-4 |
|
垂直流动方向:23℃,2.00 mm |
0.80 |
-- |
% |
|
|
流动方向:23℃,2.00 mm |
0.25 |
-- |
% |
|
|
吸水率 |
|
|
|
ISO 62 |
|
23℃,24 hr |
0.60 |
-- |
% |
|
|
平衡,23℃,50% RH |
2.0 |
-- |
% |
|
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
10000 |
5900 |
MPa |
ISO 527-2 |
|
拉伸应力(断裂,23℃) |
120 |
90.0 |
MPa |
ISO 527-2 |
|
拉伸应变(断裂,23℃) |
2.5 |
2.8 |
% |
ISO 527-2 |
|
弯曲模量(23℃) |
9000 |
4500 |
MPa |
ISO 178 |
|
弯曲应力(23℃) |
190 |
97.0 |
MPa |
ISO 178 |
|
泊松比 |
0.40 |
-- |
|
ISO 527-2 |
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
|
ISO 179 |
|
-30℃ |
3.8 |
6.0 |
kJ/m² |
|
|
23℃ |
4.4 |
10 |
kJ/m² |
|
|
简支梁无缺口冲击强度 |
|
|
|
ISO 179 |
|
-30℃ |
43 |
60 |
kJ/m² |
|
|
23℃ |
48 |
56 |
kJ/m² |
|
|
悬壁梁缺口冲击强度 |
|
|
|
ISO 180 |
|
-30℃ |
4.6 |
6.5 |
kJ/m² |
|
|
23℃ |
5.6 |
10 |
kJ/m² |
|
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
|
0.45 MPa,未退火 |
230 |
-- |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
215 |
-- |
℃ |
ISO 75-2/A |
|
熔融温度 |
255 |
-- |
℃ |
ISO 11357-3 |
|
线形热膨胀系数 |
|
|
|
ISO 11359-2 |
|
流动:23 到 55℃,2.00 mm |
2.4E-4 |
-- |
cm/cm/℃ |
|
|
横向:23 到 55℃,2.00 mm |
6.9E-4 |
-- |
cm/cm/℃ |
|
|
注射 |
干燥 |
单位制 |
||
|
干燥温度 |
80.0 |
℃ |
||
|
干燥时间 |
4.0 |
hr |
||
|
建议的最大回制料比例 |
25 |
% |
||
|
料筒后部温度 |
280 到 310 |
℃ |
||
|
料筒中部温度 |
280 到 310 |
℃ |
||
|
料筒前部温度 |
280 到 310 |
℃ |
||
|
射嘴温度 |
280 到 310 |
℃ |
||
|
加工（熔体）温度 |
285 到 305 |
℃ |
||
|
模具温度 |
65.0 到 95.0 |
℃ |
||