佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA66 R513H 加13%玻纤增强,热稳定,高强度 良好的流动性 耐化学
Vydyne® R513H
13%玻璃纤维增强材料
聚酰胺66
Ascend Performance Materials Operations LLC
产品说明:
Vydyne R513H is general-purpose, 13% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is an injection-molding grade resin that is lubricated for machine feed, flow, and mold release. Glass-reinforced Vydyne resins provide a higher heat distortion temperature, better resistance to creep, higher impact, and better dimensional stability when compared with unreinforced PA66. This product has good chemical resistance to a broad range of chemicals, including many aliphatic and aromatic hydrocarbons found in most solvents, gasoline, hydraulic fluids, greases and machine oils.
Vydyne R513H has tensile strength and modulus properties just below aluminum and zinc and can replace these metals in numerous applications due to an excellent balance of properties. Reduction in production costs, energy consumption and part weight are key advantages of Vydyne glass-reinforced PA66 resins over aluminum and/or zinc die-cast parts.
Vydyne R513H is heat-stabilized and formulated to minimize the oxidative and thermal degradation of the PA66 polymer when exposed to elevated temperatures for extended periods of time. Vydyne R513H provides improved retention of physical properties under exposure to long-term heat. The continuous operating use temperature is 275℉, with short-term peak temperatures as high as 475℉.
Typical Applications/End Uses:
Vydyne R513H resin has been used for many under-the-hood automotive applications, motor housings for power tools and garden appliances. This resin has also been used in miscellaneous brackets, gears and clips, which require high rigidity and strength.
黄卡下载：E70062-249082
填料增强：含13%玻璃纤维增强
含添加剂：润滑剂，热稳定剂
材料特性：高刚性，高强度，抗溶剂，良好的流动性，耐化学，耐汽油，耐油，耐油脂，热稳定，润滑，脱模性能良好
材料用途：齿轮，动力/其它工具，汽车的发动机罩下的零件，外壳
加工方法：注射成型
产品外观：自然色粒子
塑料牌号：PA66 R513H
产品物性：
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
密度 |
1.23 |
-- |
g/cm³ |
ISO 1183 |
|
收缩率 |
|
|
|
ISO 294-4 |
|
垂直流动方向:23℃,2.00 mm |
1.0 |
-- |
% |
|
|
流动方向:23℃,2.00 mm |
0.50 |
-- |
% |
|
|
吸水率 |
|
|
|
ISO 62 |
|
23℃,24 hr |
1.0 |
-- |
% |
|
|
平衡,23℃,50% RH |
2.2 |
-- |
% |
|
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
6200 |
3900 |
MPa |
ISO 527-2 |
|
拉伸应力(断裂,23℃) |
115 |
75.0 |
MPa |
ISO 527-2 |
|
拉伸应变(断裂,23℃) |
3.0 |
13 |
% |
ISO 527-2 |
|
弯曲模量(23℃) |
5200 |
3150 |
MPa |
ISO 178 |
|
弯曲应力(23℃) |
165 |
106 |
MPa |
ISO 178 |
|
泊松比 |
0.40 |
-- |
|
ISO 527-2 |
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
|
ISO 179 |
|
-30℃ |
6.0 |
5.3 |
kJ/m² |
|
|
23℃ |
6.0 |
7.5 |
kJ/m² |
|
|
简支梁无缺口冲击强度 |
|
|
|
ISO 179 |
|
-30℃ |
31 |
37 |
kJ/m² |
|
|
23℃ |
38 |
42 |
kJ/m² |
|
|
悬壁梁缺口冲击强度 |
|
|
|
ISO 180 |
|
-30℃ |
5.0 |
5.4 |
kJ/m² |
|
|
23℃ |
5.1 |
8.5 |
kJ/m² |
|
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
|
0.45 MPa,未退火 |
258 |
-- |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
240 |
-- |
℃ |
ISO 75-2/A |
|
熔融温度 |
260 |
-- |
℃ |
ISO 11357-3 |
|
线形热膨胀系数 |
|
|
|
ISO 11359-2 |
|
流动:23 到 55℃,2.00 mm |
3.0E-5 |
-- |
cm/cm/℃ |
|
|
横向:23 到 55℃,2.00 mm |
1.1E-4 |
-- |
cm/cm/℃ |
|
|
RTI Elec |
|
|
|
UL 746 |
|
0.750 mm |
140 |
-- |
℃ |
|
|
1.50 mm |
140 |
-- |
℃ |
|
|
3.00 mm |
140 |
-- |
℃ |
|
|
RTI Imp |
|
|
|
UL 746 |
|
0.750 mm |
120 |
-- |
℃ |
|
|
1.50 mm |
120 |
-- |
℃ |
|
|
3.00 mm |
120 |
-- |
℃ |
|
|
RTI |
|
|
|
UL 746 |
|
0.750 mm |
125 |
-- |
℃ |
|
|
1.50 mm |
140 |
-- |
℃ |
|
|
3.00 mm |
140 |
-- |
℃ |
|
|
电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
体积电阻率(0.750 mm) |
1.0E+13 |
-- |
ohm·cm |
IEC 60093 |
|
介电强度(1.00 mm) |
20 |
-- |
kV/mm |
IEC 60243 |
|
耐电弧性(3.00 mm) |
PLC 6 |
-- |
|
ASTM D495 |
|
漏电起痕指数(3.00 mm) |
250 到 399 |
-- |
V |
IEC 60112 |
|
高电弧燃烧指数(HAI) |
|
|
|
UL 746 |
|
0.750 mm |
PLC 0 |
-- |
|
|
|
1.50 mm |
PLC 0 |
-- |
|
|
|
3.00 mm |
PLC 0 |
-- |
|
|
|
高电压电弧起痕速率 (HVTR) |
PLC 1 |
-- |
|
UL 746 |
|
热丝引燃 (HWI) |
|
|
|
UL 746 |
|
0.750 mm |
PLC 4 |
-- |
|
|
|
1.50 mm |
PLC 3 |
-- |
|
|
|
3.00 mm |
PLC 4 |
-- |
|
|
|
可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
|
UL 94 |
|
0.750 mm |
HB |
-- |
|
|
|
1.50 mm |
HB |
-- |
|
|
|
3.00 mm |
HB |
-- |
|
|
|
灼热丝易燃指数 |
|
|
|
IEC 60695-2-12 |
|
0.750 mm |
675 |
-- |
℃ |
|
|
1.50 mm |
675 |
-- |
℃ |
|
|
3.00 mm |
675 |
-- |
℃ |
|
|
热灯丝点火温度 |
|
|
|
IEC 60695-2-13 |
|
0.750 mm |
700 |
-- |
℃ |
|
|
1.50 mm |
700 |
-- |
℃ |
|
|
3.00 mm |
700 |
-- |
℃ |
|
|
极限氧指数 |
25 |
-- |
% |
ISO 4589-2 |
|
注射 |
干燥 |
单位制 |
||
|
干燥温度 |
80.0 |
℃ |
||
|
干燥时间 |
4.0 |
hr |
||
|
建议的最大回制料比例 |
25 |
% |
||
|
料筒后部温度 |
280 到 310 |
℃ |
||
|
料筒中部温度 |
280 到 310 |
℃ |
||
|
料筒前部温度 |
280 到 310 |
℃ |
||
|
射嘴温度 |
280 到 310 |
℃ |
||
|
加工（熔体）温度 |
285 到 305 |
℃ |
||
|
模具温度 |
65.0 到 95.0 |
℃ |
||