PA66 R413H BK07 加13%玻璃纤增强,高刚性 耐油脂 易脱模
Vydyne® R413H BK07
13%玻璃纤维增强材料
聚酰胺66
Ascend Performance Materials Operations LLC
产品说明:
Vydyne R413H BK07 is general-purpose, heat-stabilized, impact-modified, 13% glass-fiber reinforced PA66 resin. Available in black, It is specifically designed to maximize toughness, while retaining physical properties. This product is also lubricated for improved flow and offers superior surface appearance.
Glass-fiber reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Typical Applications/End Uses:
Vydyne R413H BK07 is successfully used in a wide range of injection-molding engineering applications, including automotive clips, fasteners, brackets and carbon canisters; electrical connectors, housings, bobbins, etc.; and industrial gears, bearing shells, covers, housings, etc.
黄卡下载：E70062-101337332
填料增强：含13%玻璃纤维增强
含添加剂：润滑剂
材料特性：尺寸稳定，高刚性，高拉伸强度，高强度，抗溶剂，抗撞击，抗蠕变，流动性佳，耐化学，耐汽油，耐油脂，润滑，易脱模
材料用途：草坪和园林设备，齿轮，动力/其它工具，汽车的发动机罩下的零件，外壳
加工方法：注射成型
产品外观：黑色粒子
塑料牌号：PA66 R413H BK07
产品物性：
|
物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
密度 |
1.21 |
-- |
g/cm³ |
ISO 1183 |
|
收缩率 |
|
|
|
ISO 294-4 |
|
垂直流动方向:23℃,2.00 mm |
0.80 |
-- |
% |
|
|
流动方向:23℃,2.00 mm |
0.70 |
-- |
% |
|
|
吸水率 |
|
|
|
ISO 62 |
|
23℃,24 hr |
1.0 |
-- |
% |
|
|
平衡,23℃,50% RH |
1.9 |
-- |
% |
|
|
机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
5500 |
4100 |
MPa |
ISO 527-2 |
|
拉伸应力(断裂,23℃) |
110 |
80.0 |
MPa |
ISO 527-2 |
|
拉伸应变(断裂,23℃) |
5.0 |
13 |
% |
ISO 527-2 |
|
弯曲模量(23℃) |
4800 |
2800 |
MPa |
ISO 178 |
|
弯曲应力(23℃) |
140 |
73.0 |
MPa |
ISO 178 |
|
泊松比 |
0.40 |
-- |
|
ISO 527-2 |
|
冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
|
ISO 179 |
|
-40℃ |
5.0 |
5.0 |
kJ/m² |
|
|
-30℃ |
6.0 |
10 |
kJ/m² |
|
|
23℃ |
12 |
18 |
kJ/m² |
|
|
简支梁无缺口冲击强度 |
|
|
|
ISO 179 |
|
-30℃ |
80 |
70 |
kJ/m² |
|
|
23℃ |
75 |
76 |
kJ/m² |
|
|
悬壁梁缺口冲击强度 |
|
|
|
ISO 180 |
|
-40℃ |
9.0 |
9.0 |
kJ/m² |
|
|
-30℃ |
10 |
10 |
kJ/m² |
|
|
23℃ |
12 |
21 |
kJ/m² |
|
|
热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
热变形温度 |
|
|
|
|
|
0.45 MPa,未退火 |
258 |
-- |
℃ |
ISO 75-2/B |
|
1.8 MPa,未退火 |
235 |
-- |
℃ |
ISO 75-2/A |
|
熔融温度 |
260 |
-- |
℃ |
ISO 11357-3 |
|
线形热膨胀系数 |
|
|
|
ISO 11359-2 |
|
流动:23 到 55℃,2.00 mm |
3.0E-5 |
-- |
cm/cm/℃ |
|
|
横向:23 到 55℃,2.00 mm |
1.1E-4 |
-- |
cm/cm/℃ |
|
|
电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
体积电阻率(0.750 mm) |
1.0E+9 |
-- |
ohm·cm |
IEC 60093 |
|
介电强度(1.00 mm) |
3.0 |
-- |
kV/mm |
IEC 60243 |
|
耐电弧性(3.00 mm) |
PLC 6 |
-- |
|
ASTM D495 |
|
漏电起痕指数(3.00 mm) |
400 到 599 |
-- |
V |
IEC 60112 |
|
高电弧燃烧指数(HAI) |
|
|
|
UL 746 |
|
0.400 mm |
PLC 1 |
-- |
|
|
|
0.750 mm |
PLC 1 |
-- |
|
|
|
1.50 mm |
PLC 1 |
-- |
|
|
|
3.00 mm |
PLC 1 |
-- |
|
|
|
高电压电弧起痕速率 (HVTR) |
PLC 3 |
-- |
|
UL 746 |
|
热丝引燃 (HWI) |
|
|
|
UL 746 |
|
0.400 mm |
PLC 4 |
-- |
|
|
|
0.750 mm |
PLC 4 |
-- |
|
|
|
1.50 mm |
PLC 4 |
-- |
|
|
|
3.00 mm |
PLC 4 |
-- |
|
|
|
可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
|
UL 阻燃等级 |
|
|
|
UL 94 |
|
0.750 mm |
HB |
-- |
|
|
|
1.50 mm |
HB |
-- |
|
|
|
3.00 mm |
HB |
-- |
|
|
|
注射 |
干燥 |
单位制 |
||
|
干燥温度 |
80.0 |
℃ |
||
|
干燥时间 |
4.0 |
hr |
||
|
建议的最大回制料比例 |
25 |
% |
||
|
料筒后部温度 |
280 到 310 |
℃ |
||
|
料筒中部温度 |
280 到 310 |
℃ |
||
|
料筒前部温度 |
280 到 310 |
℃ |
||
|
射嘴温度 |
280 到 310 |
℃ |
||
|
加工（熔体）温度 |
285 到 305 |
℃ |
||
|
模具温度 |
65.0 到 95.0 |
℃ |
||