佳 盼 塑 胶
JIA PAN SU JIAO
/ Product details
/ classification
PA66 50BW,50BWFS 耐油,抗溶解
ASCEND Vydyne PA66 50BW & 50BWFS
Vydyne® 50BWFS is a general purpose Nylon 66 resin. Available in natural. Designed for extrusion applications that do not require use of a highviscosity resin. This resin offers a well-balanced combination of engineering properties characterized by high strength, rigidity, good toughness, high melt point, good surface lubricity, and abrasion resistance. Vydyne 50BWFS maintains the chemical resistance typical of nylon to many chemicals, solvents, gasoline, and machine and motor oils. This resin is manufactured as an undried feedstock with a maximum moisture level of 0.5%.
Vydyne 50BWFS permits the manufacturing of parts with good initial color plus good property and color retention when using regrind. This resin is recognized by Underwriters Laboratories and conforms to the requirements of many industrial, federal, and military specifications for premium-quality general purpose Nylon 66 resins.
Typical Applications/End Uses
Vydyne 50BWFS has been successfully extruded in applications that do not require high melt strength, such as monofilament and bristle products.
产品牌号: PA66 50BW,50BWFS
产品物性:
|
50BWFS 物理性能 |
额定值 |
单位制 |
测试方法 |
|
密度 |
1.14 |
g/cm³ |
ISO 1183 |
|
表观密度 |
0.67 |
g/cm³ |
ASTM D1895 |
|
Viscosity Number(Reduced Viscosity)2 |
45.0到51.0 |
ml/g |
ASTM D789 |
|
粘数(H2SO4(硫酸)) |
136到143 |
cm³/g |
ISO 307 |
|
含水量 |
0.50 |
% |
ASTM D789 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
熔融温度 |
260 |
℃ |
ISO 11357-3 |
|
光学性能 |
额定值 |
单位制 |
测试方法 |
|
黄度指数 |
< 0.0 |
YI |
ASTM D1925 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
70.0 |
℃ |
|
|
干燥时间 |
1.0到3.0 |
hr |
|
|
建议注入量 |
40到80 |
% |
|
|
建议的最大回制料比例 |
25 |
% |
|
|
螺筒后部温度 |
270到310 |
℃ |
|
|
螺筒中部温度 |
270到310 |
℃ |
|
|
螺筒前部温度 |
270到310 |
℃ |
|
|
加工(熔体)温度 |
275到305 |
℃ |
|
|
模具温度 |
15.0到95.0 |
℃ |
|
|
注塑温度 |
55.0到140 |
MPa |
|
|
注射速度 |
快速 |
|
|
|
保压 |
55.0到140 |
MPa |
|
|
背压 |
0.200到1.00 |
MPa |
|
|
螺杆转速 |
50到150 |
rpm |
|
|
合模力 |
2.7到6.2 |
kN/cm² |
|
|
垫层 |
3.00到6.40 |
mm |
|
|
注射说明 |
|||
|
50BW 物理性能 |
额定值 |
单位制 |
测试方法 |
|
密度 |
1.14 |
g/cm³ |
ISO 1183 |
|
表观密度 |
0.67 |
g/cm³ |
ASTM D1895 |
|
Viscosity Number (Reduced Viscosity)2 |
45.0 到 51.0 |
ml/g |
ASTM D789 |
|
粘数(H2SO4(硫酸)) |
136 到 146 |
cm³/g |
ISO 307 |
|
含水量 |
< 0.20 |
% |
ASTM D789 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
熔融温度 |
260 |
℃ |
ISO 11357-3 |
|
光学性能 |
额定值 |
单位制 |
测试方法 |
|
黄度指数 |
< 0.0 |
YI |
ASTM D1925 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
70 |
℃ |
|
|
干燥时间 |
1.0 到 3.0 |
hr |
|
|
建议注入量 |
40 到 80 |
% |
|
|
建议的最大回制料比例 |
25 |
% |
|
|
螺筒后部温度 |
270 到 310 |
℃ |
|
|
螺筒中部温度 |
270 到 310 |
℃ |
|
|
螺筒前部温度 |
270 到 310 |
℃ |
|
|
射嘴温度 |
270 到 310 |
℃ |
|
|
加工(熔体)温度 |
275 到 305 |
℃ |
|
|
模具温度 |
15.0 到 95.0 |
℃ |
|
|
注塑温度 |
55.0 到 140 |
MPa |
|
|
注射速度 |
快速 |
|
|
|
保压 |
55.0 到 140 |
MPa |
|
|
背压 |
0.200 到 1.00 |
MPa |
|
|
螺杆转速 |
50 到 150 |
rpm |
|
|
合模力 |
2.7 到 6.2 |
kN/cm² |
|
|
垫层 |
3.00 到 6.40 |
mm |
|
|
注射说明 |
|||
|
挤出 |
额定值 |
单位制 |
|
|
干燥温度 |
70 |
℃ |
|
|
干燥时间 |
1.0 到 3.0 |
hr |
|
|
第1气缸区温度 |
270 到 310 |
℃ |
|
|
第2气缸区温度 |
270 到 310 |
℃ |
|
|
第3气缸区温度 |
270 到 310 |
℃ |
|
|
第4气缸区温度 |
270 到 310 |
℃ |
|
|
第5气缸区温度 |
270 到 310 |
℃ |
|
|
熔体温度 |
275 到 305 |
℃ |
|