PA66 A3W BK00464 抗热老化,流动性好,耐油，生产阶段快
Ultramid® PA66 A3W BK00464
聚酰胺66
BASF Corporation
产品说明
Ultramid A3W BK00464 is an easy flowing, pigmented black, heat aging resistant injection molding PA66 grade for fast processing.
Applications
Typical applications include highly stressed parts such as bearings, bearing cages, gear-wheels, coil formers and cable connectors.
UL 黄卡2：E36632-531628
材料特点：抗热老化，流动性好，耐油，生产阶段快
产品用途：Electrical Housing，齿轮，电气部件，工程配件，工业领域，连接器，汽车电子，汽车领域的应用，轴承
外观颜色：黑色
产品形式：颗粒料
加工方法：注射成型
塑料牌号：PA66 A3W BK00464
定属记号：尼龙66
物料数据
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.14 |
g/cm³ |
ASTM D792,ISO 1183 |
|
吸水率 |
|
|
|
|
饱和 |
8.5 |
% |
ASTM D570 |
|
饱和,23℃ |
8.5 |
% |
ISO 62 |
|
平衡,50% RH |
2.8 |
% |
ASTM D570 |
|
平衡,23℃,50% RH |
2.8 |
% |
ISO 62 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
3300 |
MPa |
ISO 527-2 |
|
抗张强度 |
|
|
|
|
屈服,23℃ |
85.0 |
MPa |
ASTM D638 |
|
屈服,23℃ |
88.0 |
MPa |
ISO 527-2 |
|
伸长率 |
|
|
|
|
屈服,23℃ |
4.5 |
% |
ASTM D638 |
|
屈服,23℃ |
4.7 |
% |
ISO 527-2 |
|
弯曲模量(23℃) |
3100 |
MPa |
ISO 178 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
ISO 179 |
|
-30℃ |
3.0 |
kJ/m² |
|
|
23℃ |
4.6 |
kJ/m² |
|
|
悬壁梁缺口冲击强度 |
|
|
|
|
-40℃ |
48 |
J/m |
ASTM D256 |
|
23℃ |
53 |
J/m |
ASTM D256 |
|
-40℃ |
4.0 |
kJ/m² |
ISO 180 |
|
23℃ |
4.5 |
kJ/m² |
ISO 180 |
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度(1.8 MPa,未退火) |
75.0 |
℃ |
ISO 75-2/A |
|
熔融峰值温度 |
260 |
℃ |
ASTM D3418,ISO 3146 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
80.0 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.20 |
% |
|
|
加工（熔体）温度 |
280 到 300 |
℃ |
|
|
模具温度 |
40.0 到 80.0 |
℃ |
|
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
|
|
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.