PA66 66 H2 G/35-V0KB NAT0046 含35%玻璃纤维增强,电气性能佳，流动性好，热稳定，自熄，阻燃级
Ultramid® PA66 66 H2 G/35-V0KB NAT0046
聚酰胺66
玻璃纤维增强材料,35%
BASF Corporation
产品说明
Ultramid 66 H2 G/35-V0KB NAT0046 is a 35% glass reinforced, heat stabilized injection molding grade. It is a V-0 self-extinguishing grade, with phosphorous. It offers good flowability and mechanical properties. It has excellent electrical properties.
Ultramid 66H2 G/35-V0KB NAT0046 is designed for applications requiring good processing, mechanical integrity and flammability performance.
黄卡下载：E36632-100101020
填料增强：含35%玻璃纤维增强材料
含添加剂：热稳定剂，阻燃3
材料特点：可加工性好，电气性能佳，流动性好，热稳定，自熄，阻燃级
外观颜色：自然色
外观形式：颗粒料
加工方法：注射成型
塑料牌号：PA66 66 H2 G/35-V0KB NAT0046
定属记号：尼龙66
物料数据
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
密度 |
1.45 |
g/cm³ |
ISO 1183 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量(23℃) |
11300 |
MPa |
ISO 527-2 |
|
拉伸应力(断裂,23℃) |
175 |
MPa |
ISO 527-2 |
|
拉伸应变(断裂,23℃) |
2.7 |
% |
ISO 527-2 |
|
弯曲模量(23℃) |
10700 |
MPa |
ISO 178 |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
简支梁缺口冲击强度 |
|
|
ISO 179 |
|
-30℃ |
9.0 |
kJ/m² |
|
|
23℃ |
10 |
kJ/m² |
|
|
悬壁梁缺口冲击强度 |
|
|
ISO 180 |
|
-40℃ |
9.0 |
kJ/m² |
|
|
23℃ |
10 |
kJ/m² |
|
|
热性能 |
额定值 |
单位制 |
测试方法 |
|
热变形温度(1.8 MPa,未退火) |
247 |
℃ |
ISO 75-2/A |
|
溶融温度（DSC） |
260 |
℃ |
ISO 3146 |
|
可燃性 |
额定值 |
|
测试方法 |
|
UL 阻燃等级 |
V-0 |
|
UL 94 |
|
注射 |
额定值 |
单位制 |
|
|
干燥温度 |
80.0 |
℃ |
|
|
干燥时间 |
2.0 到 4.0 |
hr |
|
|
建议的最大水分含量 |
0.050 |
% |
|
|
加工（熔体）温度 |
285 到 300 |
℃ |
|
|
模具温度 |
80.0 到 90.0 |
℃ |
|
|
注塑压力 |
3.50 到 12.5 |
MPa |
|
|
注射速度 |
快速 |
|
|
|
备注: |
|||
Ultramid® polyamides are molding compounds based on PA 6, PA 66 and copolyamides such as PA 66/6. Due to their outstanding properties these materials have become indispensable in almost all fields of engineering for the most varied components and machine parts, as high-quality electrical insulating materials and for many special applications.