PA66 RX89047 compound 含专有填料
LNP™ VERTON™ PA66 RX89047 compound
聚酰胺66
专有填料
SABIC Innovative Plastics (Americas)
产品说明
Also known as:LNP™ VERTON™ Compound PDX-R-89047
Product reorder name:RX89047
LNP* VERTON* RX89047 is a compound based on Nylon 66 resin containing Proprietary Fillers. Added feature of this grade is: Structural.
增强填料：含专有填料
塑料牌号：PA66 RX89047
定属记号：尼龙66
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,break |
2050 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain,break |
2.3 |
% |
ASTM D 638 |
|
Tensile Modulus,50 mm/min |
116000 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress |
3230 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus |
98400 |
kgf/cm² |
ASTM D 790 |
|
Tensile Stress,break |
198 |
MPa |
ISO 527 |
|
Tensile Strain,break |
198 |
% |
ISO 527 |
|
Flexural Modulus |
9500 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched,23℃ |
103 |
cm-kgf/cm |
ASTM D 4812 |
|
Izod Impact,notched,23℃ |
36 |
cm-kgf/cm |
ASTM D 256 |
|
Izod Impact,notched 80*10*4 +23℃ |
24 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT,1.82 MPa,3.2mm,unannealed |
253 |
℃ |
ASTM D 648 |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
251 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.42 |
g/cm³ |
ASTM D 792 |
|
Density |
1.41 |
g/cm³ |
ISO 1183 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
280-305 |
℃ |
|
|
Front-Zone 3 Temperature |
295-305 |
℃ |
|
|
Middle-Zone 2 Temperature |
280-295 |
℃ |
|
|
Rear-Zone 1 Temperature |
265-275 |
℃ |
|
|
Mold Temperature |
95-110 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.