PA66 RX07013 含长玻璃纤维,易成型,抗紫外线稳定
LNP™ VERTON™ PA66 RX07013 compound
聚酰胺66
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle)
LNP VERTON * RX07013 is a compound based on Nylon 66 resin containig Long Glass. Added features of this material include: Easy Molding and UV Resistant.
增强填料：含长玻璃纤维
材料特点：易成型,抗紫外线稳定
塑料牌号：PA66 RX07013
定属记号：尼龙66
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,break,5 mm/min |
265 |
MPa |
ISO 527 |
|
Tensile Strain,break,5 mm/min |
1.9 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
18380 |
MPa |
ISO 527 |
|
Flexural Modulus,2 mm/min |
15550 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,unnotched 80*10*4 +23℃ |
89 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
45 |
kJ/m² |
ISO 180/1A |
|
Izod Impact,notched 80*10*4 -40℃ |
38 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
CTE,-40℃ to 40℃,flow |
1.86E-05 |
1/℃ |
ISO 11359-2 |
|
CTE,-40℃ to 40℃,xflow |
6.73E-05 |
1/℃ |
ISO 11359-2 |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
258 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
253 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.58 |
g/cm³ |
ISO 1183 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
290-305 |
℃ |
|
|
Front-Zone 3 Temperature |
290-300 |
℃ |
|
|
Middle-Zone 2 Temperature |
290-300 |
℃ |
|
|
Rear-Zone 1 Temperature |
280-295 |
℃ |
|
|
Mold Temperature |
95-110 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.