PA66 RX06424 含60%长玻璃纤维,易成型,热稳定,抗紫外线
LNP™ VERTON™ PA66 RX06424 compound
聚酰胺66
60%长玻璃纤维
SABIC Innovative Plastics (Americas)
产品说明
Also known as:LNP™ VERTON™ Compound RF-700-12 EM HS UV
Product reorder name:RX06424
LNP VERTON* RX06424 is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, UV Stabilized, Structural
增强填料：含60%长玻璃纤维
材料特点：易成型,热稳定,抗紫外线
定属记号：尼龙66
塑料牌号：PA66 RX06424
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,break |
2750 |
kgf/cm² |
ASTM D 638 |
|
Tensile Strain,break |
1.6 |
% |
ASTM D 638 |
|
Tensile Modulus,50 mm/min |
200300 |
kgf/cm² |
ASTM D 638 |
|
Flexural Stress |
4380 |
kgf/cm² |
ASTM D 790 |
|
Flexural Modulus |
183800 |
kgf/cm² |
ASTM D 790 |
|
Tensile Stress,break |
261 |
MPa |
ISO 527 |
|
Tensile Strain,break |
1.6 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
23280 |
MPa |
ISO 527 |
|
Flexural Stress |
433 |
MPa |
ISO 178 |
|
Flexural Modulus |
18920 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Izod Impact,notched,23℃ |
42 |
cm-kgf/cm |
ASTM D 256 |
|
Instrumented Impact Energy @ peak,23℃ |
183 |
cm-kgf |
ASTM D 3763 |
|
Multiaxial Impact |
183 |
cm-kgf |
ISO 6603 |
|
Izod Impact,unnotched 80*10*4 +23℃ |
102 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
54 |
kJ/m² |
ISO 180/1A |
|
Izod Impact,notched 80*10*4 -40℃ |
43 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT,1.82 MPa,3.2mm,unannealed |
247 |
℃ |
ASTM D 648 |
|
CTE,-40℃ to 40℃,flow |
1.76E-05 |
1/℃ |
ASTM E 831 |
|
CTE,-40℃ to 40℃,xflow |
5.36E-05 |
1/℃ |
ASTM E 831 |
|
CTE,-40℃ to 40℃,flow |
1.7E-05 |
1/℃ |
ISO 11359-2 |
|
CTE,-40℃ to 40℃,xflow |
5.3E-05 |
1/℃ |
ISO 11359-2 |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
252 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
252 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Density |
1.71 |
g/cm³ |
ASTM D 792 |
|
Moisture Absorption,50% RH,24 hrs |
0.44 |
% |
ASTM D 570 |
|
Mold Shrinkage,flow,24 hrs (5) |
0.2 |
% |
ASTM D 955 |
|
Mold Shrinkage,xflow,24 hrs (5) |
0.4 |
% |
ASTM D 955 |
|
Mold Shrinkage,flow,24 hrs (5) |
0.2 |
% |
ISO 294 |
|
Mold Shrinkage,xflow,24 hrs (5) |
0.4 |
% |
ISO 294 |
|
Density |
1.71 |
g/cm³ |
ISO 1183 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
290-305 |
℃ |
|
|
Front-Zone 3 Temperature |
290-300 |
℃ |
|
|
Middle-Zone 2 Temperature |
290-300 |
℃ |
|
|
Rear-Zone 1 Temperature |
280-295 |
℃ |
|
|
Mold Temperature |
95-110 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.