PA66 RX03013 含长玻纤和润滑油
LNP™ VERTON™ PA66 RX03013 compound
聚酰胺66
长玻璃纤维
SABIC Innovative Plastics (Europe-Africa-Middle)
产品说明
Also known as:LNP™ VERTON™ Compound PDXR03013-NAT
Product reorder name:RX03013
LNP* VERTON* RX03013 is a compound based on PA 66 resin containing Long Glass Fiber, Proprietary Lubricant. Added features include: Internally Lubricated.
增强填料：含长玻璃纤维
含添加剂：专用润滑油
材料特点：内部润滑
塑料牌号：PA66 RX03013
定属记号：尼龙66
加工方法：注射成型
材料物性
|
MECHANICAL |
Value |
Unit |
Standard |
|
Tensile Stress,break,5 mm/min |
205 |
MPa |
ISO 527 |
|
Tensile Strain,break,5 mm/min |
2.2 |
% |
ISO 527 |
|
Tensile Modulus,1 mm/min |
12500 |
MPa |
ISO 527 |
|
Flexural Stress,break,2 mm/min |
307 |
MPa |
ISO 178 |
|
Flexural Strain,break,2 mm/min |
3.1 |
% |
ISO 178 |
|
Flexural Modulus,2 mm/min |
10800 |
MPa |
ISO 178 |
|
IMPACT |
Value |
Unit |
Standard |
|
Multiaxial Impact |
59 |
cm-kgf |
ISO 6603 |
|
Izod Impact,unnotched 80*10*4 +23℃ |
70 |
kJ/m² |
ISO 180/1U |
|
Izod Impact,notched 80*10*4 +23℃ |
28 |
kJ/m² |
ISO 180/1A |
|
THERMAL |
Value |
Unit |
Standard |
|
HDT/Bf,0.45 MPa Flatw 80*10*4 sp=64mm |
265 |
℃ |
ISO 75/Bf |
|
HDT/Af,1.8 MPa Flatw 80*10*4 sp=64mm |
261 |
℃ |
ISO 75/Af |
|
PHYSICAL |
Value |
Unit |
Standard |
|
Mold Shrinkage,flow,24 hrs(5) |
0.4 |
% |
ISO 294 |
|
Mold Shrinkage,xflow,24 hrs(5) |
0.9 |
% |
ISO 294 |
|
Density |
1.44 |
g/cm³ |
ISO 1183 |
|
Water Absorption,23℃/24hrs |
1.1 |
% |
ISO 62-1 |
|
Injection Molding |
Value |
Unit |
|
|
Drying Temperature |
80 |
℃ |
|
|
Drying Time |
4 |
hrs |
|
|
Maximum Moisture Content |
0.15-0.25 |
% |
|
|
Melt Temperature |
290-305 |
℃ |
|
|
Front-Zone 3 Temperature |
290-300 |
℃ |
|
|
Middle-Zone 2 Temperature |
290-300 |
℃ |
|
|
Rear-Zone 1 Temperature |
280-295 |
℃ |
|
|
Mold Temperature |
95-110 |
℃ |
|
|
Back Pressure |
0.2-0.3 |
MPa |
|
|
Screw Speed |
30-60 |
rpm |
|
PA66 LNP™ VERTON™ COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.